A high-strength hot-dip galvanized steel sheet having a surface coated with a hot-dip galvanized coating, the steel sheet having a chemical composition comprising C: more than 0.10% and less than 0.18%, Si: 0.01 to 1.00%, Mn: 1.5 to 4.0%, P: 0.100% or less, S: 0.020% or less, Al: 0.010 to 0.500%, Cr: 0.010 to 2.000%, Nb: 0.005 to 0.100%, Ti: 0.005 to 0.100%, B: more than 0.0005% and 0.0030% or less, and Fe and incidental impurities, and a method for producing the same. The steel sheet has a microstructure including ferrite having an area fraction in the range of 0 to 10%, martensite having an area fraction in the range of 15 to 60%, tempered martensite having an area fraction in the range of 20 to 50%, and bainitic ferrite having an area fraction in the range of 20 to 50%.