A heat-resistant cold rolled ferritic stainless steel sheet containing, in mass %, 0.02% or less of C, 0.1% to 1.0% of Si, greater than 0.6% to 1.5% of Mn, 0.01% to 0.05% of P, 0.0001% to 0.0100% of S, 13.0% to 20.0% of Cr, 0.1% to 3.0% of Mo, 0.005% to 0.20% of Ti, 0.3% to 1.0% of Nb, 0.0002% to 0.0050% of B, 0.005% to 0.50% of Al, 0.02% or less of N, with the balance being Fe and inevitable impurities, in which {111}-oriented grains are present at an area ratio of 20% or greater in a region from a surface layer to t/4 (t is a sheet thickness), {111}-oriented grains are present at an area ratio of 40% or greater in a region from t/4 to t/2, and {011}-oriented grains are present at an area ratio of 15% or less in the entire region in a thickness direction.