An aluminum alloy brazing sheet achieves a stable brazability equal to by brazing using a flux, even if an etching treatment is not performed on the brazing site. The aluminum alloy brazing sheet is used to braze aluminum in an inert gas atmosphere without using a flux and includes a core material and a filler metal, one side or each side of the core material being clad with the filler metal, the core material being formed of an aluminum alloy that includes 0.2 to 1.3 mass % of Mg, the filler metal including 6 to 13 mass % of Si and 0.004 to 0.1 mass % of Li, with the balance being aluminum and unavoidable impurities, a surface oxide film having been removed from the brazing sheet, and an oil solution that decomposes when heated at 380° C. or less in an inert gas having been applied to the brazing sheet.