Superhydrophilic and antifogging non-porous TiO2 films for glass substrates and methods of providing the TiO2 films are provided. The TiO2 films may maintain a water contact angle less than 5° in the dark for five days after an annealing treatment, and the water contact angle of the TiO2 films may stabilize at less than 20° after ten days from the annealing treatment. The TiO2 films may have a thickness of about 20 nm and may be transparent. The methods may include depositing a TiO2 film on a glass substrate using e-beam evaporation. The methods may further include annealing the TiO2 film after depositing the TiO2 film on the glass substrate. The methods may not include UV radiation.