Disclosed is a method for melting and solidification of a scintillating material in micromechanical structures, including controlling the melting and solidification of the scintillating material by individually controlled heat sources, a top heater and a bottom heater, placed above and below a process chamber, housing a sample with the micromechanical structures and the scintillating material. The heaters are controlled to set a vertical temperature gradient over the sample to control the melting and solidification of the scintillating material. During melting, the top heater is ramped up and stabilized at a temperature where no melting occurs and the bottom heater is ramped up and stabilized at a temperature where melting occurs during a period of time while the scintillating material melts and flows into the micromechanical structures. During solidification, the temperature of the bottom heater decreases to enable solidification to take place starting from the bottom of the micromechanical structures.