A method for producing a dielectric ceramic includes: shaping mixed powdery particles including a cordierite material (2MgO.2Al2O3.5SiO2) and a low-temperature-sintering material including Al, Si and Sr, the Si being partially vitrified; and firing the resultant shaped body. The method includes the step of wet-pulverizing the low-temperature-sintering material together with at least the cordierite material to prepare mixed powder particles having a median diameter D50 less than 1 μm; and, in a process until a time of the preparation of the mixed powder particles, the low-temperature-sintering material undergoes no step of wet-pulverizing only the low-temperature-sintering material, and drying the resultant pulverized material.