The invention provides a method of improving the corrosion resistance of a metal substrate. The method comprises: (a) electrophoretically depositing on the substrate a curable electrodepositable coating composition to form a coating over at least a portion of the substrate, and (b) heating the substrate to a temperature and for a time sufficient to cure the coating on the substrate. The electrodepositable coating composition comprises a resinous phase dispersed in an aqueous medium, the resinous phase comprising: (1) an ungelled active hydrogen-containing, cationic salt group-containing resin electrodepositable on a cathode; (2) an at least partially blocked polyisocyanate curing agent; and (3) a pigment component comprising an inorganic, platelike pigment having an average equivalent spherical diameter of at least 0.2 microns. The electrodepositable coating composition demonstrates a pigment-to-binder ratio of at least 0.5. The coating composition contains less than 8 percent by weight of a grind vehicle.