Provided are a steel sheet with excellent weldability, and a production method therefor.The steel sheet is characterized by having a specific composition and a metallographic structure containing, in terms of an area ratio, ferrite of 25% or more and 65% or less, martensite having iron-based carbides precipitated in the grains of 35% or more and 75% or less, and the balance structure other than the ferrite and the martensite of 20% or less (including 0%) in total, the average grain diameters of the ferrite and the martensite being respectively 5 μm or lower, the total of concentration of Si and Mn at interface between the ferrite and the martensite being, in terms of an atomic concentration, 5% or more, and having a tensile strength of 900 MPa or higher.