A nitrided steel part excellent in pitting resistance and bending fatigue characteristic enabling reduction of size and decrease of weight of parts or enabling demand for high load capacities to be met, using as a material a steel material containing, by mass %, C: 0.05 to 0.25%, Si: 0.05 to 1.5%, Mn: 0.2 to 2.5%, P: 0.025% or less, S: 0.003 to 0.05%, Cr: over 0.5 to 2.0%, Al: 0.01 to 0.05%, and N: 0.003 to 0.025%, having a balance of Fe and impurities, having formed on the steel surface a compound larger of a thickness 3 μm or less containing iron, nitrogen, and carbon and a hardened layer formed below the compound layer, and having an effective hardened layer depth of 160 to 410 μm.