Provided is a magnesium oxide-containing spinel powder capable of producing a ceramic sintered body having high strength and excellent strength stability. In the magnesium oxide-containing spinel powder, a 50% particle diameter (D50) is 0.30 to 10.00 μm, a ratio (D90-D50)/(D50-D10) of a difference between a 90% particle diameter (D90) and the 50% particle diameter (D50) and a difference between the 50% particle diameter (D50) and a 10% particle diameter (D10) is 1.0 to 5.0, and a composition ratio of Mg and Al in terms of an oxide equivalent content is 50 to 90% by weight of MgO and 10 to 50% by weight of Al2O3.