The instant disclosure relates to a method for manufacturing a transparent polyimide film, including providing a polyamic acid solution having a fluorine content more than 12%; adding a dehydrating agent and a catalyst into the polyamic acid solution, the dehydrating agent having an equivalent number equal to or larger than 3; and baking the polyamic acid solution under a temperature ranging from 250 to 350° C. for performing a chemical imidization process so that the transparent polyimide film is obtained. The transparent polyimide film has an elongation rate of more than 30% and a b* value in a CIELAB coordinate of less than 3.5.