A method for manufacturing a grain-oriented electrical steel sheet, according to an embodiment of the present invention includes: heating a slab, based on 100 wt % of a total composition thereof, including N at 0.0005 wt % to 0.015 wt %, Ti at 0.0001 wt % to 0.020 wt %, V at 0.0001 wt % to 0.020 wt %, Nb at 0.0001 wt % to 0.020 wt %, B at 0.0001 wt % to 0.020 wt %, and the remaining portion including Fe and other impurities, and then hot rolling it to prepare a hot-rolled steel sheet; annealing the hot-rolled steel sheet; after the hot-rolled steel sheet is annealed, cooling the hot-rolled steel sheet, and then cold rolling it to prepare a cold-rolled steel sheet; decarburization-annealing the cold-rolled steel sheet and then nitriding-annealing it, or simultaneously performing the decarburization-annealing and the nitriding-annealing; and final-annealing the decarburization-annealed and nitriding-annealed steel sheet.