A polyarylene sulfide resin particulate has a mean particle diameter from more than 1 μm to 100 the uniformity is 4 or less, the melt viscosity measured at temperature of 300° C. and shear rate of 1216 sec−1 is 150 to 500 Pa·s, and the recrystallization temperature, defined as temperature of the heat generation peak at the time of crystallization when cooled from 340° C. to 50° C. at 20° C./min using a differential scanning calorimeter, is 150 to 210° C. The polyarylene sulfide resin particulate is suitable as a material powder for producing a three-dimensional molding by a powder sintering three-dimensional printer can be provided efficiently.