The disclosure relates to a method for preparing Ti(C,N)-based superhard metal composite materials, with Ti(C,N) powder and (W,Mo,Ta)(C,N) powder as main raw materials and Co powder as binding phase for preparation, thereby obtaining a material in which a microstructure is a double-core rim structure that has both a black core rim and a white core rim. The material has a complete and evenly distributed double-core rim structure. In the condition that the ensured hardness of the material is not reduced and even slightly increased, the toughness of the material is significantly improved, wherein the fracture toughness of the material is in the range of 11.3 to 12.5 MPa·m1/2.