Non-oriented electrical steel sheet and manufacturing method therefor
Abstract:
The present invention relates to a non-oriented electrical steel sheet including 1.5 to 4.0 wt % of Si, 0.1 to 1.5 wt % of Al, 0.1 to 1.5 wt % of Mn, 0.005 wt % or less (excluding 0%) of C, 0.005 wt % or less (excluding 0%) of N, 0.005 wt % or less (excluding 0%) of Ti, 0.001 to 0.005 wt % of S, 0.1 wt % or less (excluding 0%) of P, 0.02 to 0.2 wt % of at least one of Sn and Sb, and a balance of Fe and other inevitable impurities; and satisfying the following Formulas 1, 2, and 3. 0.9≤[Al]+[Mn]≤2.1  [Formula 1] 0.2≤([Si]+[Al]+[Mn]/2)*([P]+[Sn]+[Sb])≤0.4  [Formula 2] (Gscenter−Gssurface)/(Gscenter*t)≤0.5  [Formula 3] (In Formula 1 and Formula 2, [Al], [Mn], [Si], [P], [Sn], and [Sb] represent the content (weight %) of Al, Mn, Si, P, Sn, and Sb, respectively, and
in Formula 3, t represents the thickness (mm) of the non-oriented electrical steel sheet, Gssurface represents the average grain size (μm) from 0 to t/4 or 3t/4 to t based on the thickness direction of the non-oriented steel sheet, Gscenter represents the average grain size (μm) from more than t/4 to less than 3t/4 based on the thickness direction of the non-oriented steel sheet.)
Information query
Patent Agency Ranking
0/0