A method of forming a shaped steel object is provided. The method includes cutting a blank from an alloy composition including 0.05-0.5 wt. % carbon, 4-12 wt. % manganese, 1-8 wt. % aluminum, 0-0.4 wt. % vanadium, and a remainder balance of iron. The method also includes heating the blank until the blank is austenitized to form a heated blank, transferring the heated blank to a press, forming the heating blank into a predetermined shape to form a stamped object, and decreasing the temperature of the stamped object to a temperature between a martensite start (Ms) temperature of the alloy composition and a martensite final (Mf) temperature of the alloy composition to form a shaped steel object comprising martensite and retained austenite.