The ceramic material element includes a main phase of orthorhombic perovskite-structure and a secondary phase due to a heat treatment within 700° C. to 850° C. for a first period followed by a second period within 1140° C. to 1170° C., from a mixture of materials A1, A2, A3, A4 and A5 excluding lead, the materials A1, A2, A3, A4 and A5 having molar ratios R1, R2, R3, R4 and R5, respectively, where the material A1 comprises potassium, the material A2 comprises sodium, the material A3 comprises barium, the material A4 comprises niobium, and the material A5 comprises nickel, and the molar ratio R1 is in a range 0.29-0.32, the molar ratio R2 is in a range 0.20-0.23, the molecular ratio R3 is in a range 0.01-0.02, the molar ratio R4 is in a range 0.54-0.55, and the molar ratio R5 is in a range 0.006-0.011, while a relative ratio of R1/R2 is in the range 1.24-1.52, and a relative ratio of R4/R2 is in the range 2.32-2.62. The ceramic material element converts optical radiation energy and mechanical vibration energy into electric energy.