An aspect of the present invention relates to a high strength steel sheet having an excellent high-temperature elongation characteristic, wherein the sheet comprises, by weight %, 0.4-0.9% of C, 0.01-1.5% of Cr, 0.03% or less (exclusive of 0%) of P, 0.01% or less (exclusive of 0%) of S, 0.01% or less (exclusive of 0%) of N, 0.01% or less (exclusive of 0%) of sol. Al, and a balance of Fe and inevitable impurities, and comprises at least one among 2.1% or less (exclusive of 0%) of Mn and 1.6% or less (exclusive of 0%) of Si; the sheet has a microcrystalline structure including pearlite having an area fraction of 80% or more and ferrite having an area fraction of 20% or less; and the pearlite includes cementite having a major axis length of 200 nm or shorter.