Provided is a method of manufacturing a porous polytetrafluoroethylene (PTFE) membrane capable of achieving both a high collection efficiency and a low pressure drop, though it has a larger average pore size and a greater thickness than conventional porous PTFE membranes. This manufacturing method includes: stretching an unsintered polytetrafluoroethylene sheet by a factor of 5 to 30 in a predetermined direction at a temperature equal to or higher than the melting point of polytetrafluoroethylene; further stretching the stretched sheet by a factor of 5 to 40 in a direction different from the predetermined direction at a temperature lower than the melting point; and after the stretchings, heating the stretched sheet at a temperature equal to or higher than the melting point.