A high tensile steel sheet having 980 MPa or higher tensile strength with excellent elongation and stretch-flange formability, suitable for the press-forming of complex cross sectional shape such as automobile parts, is manufactured by adjusting the steel to consist essential of a ferrite single phase structure, to precipitate carbide containing Ti, Mo, and V, of smaller than 10 nm of average particle size, in dispersed state, and to have an average composition of the carbide containing Ti, Mo, and V satisfying [V/(Ti+Mo+V)≧0.3 (atomic ratio].