A thread forming screw having a minimum surface hardness of HRC 56. The screw can form threads in a workpiece having a surface hardness which exceeds HRC 23. A method of surface hardening a screw includes carbon enriching the screw to at least a 0.48 carbon level, and then quenching the screw. Then, the screw is tempered such that the surface hardness does not exceed the core hardness by more than 3 Rockwell C points, and both the surface and core are at a Rockwell C33-C39 hardness. Subsequently, the point is induction hardened, and the screw is quenched again. The screw is again tempered such that the lead threads and the first 3-4 full threads are at a Rockwell C56 minimum hardness, preferably to a depth of at least 0.008 inches, and the core of the fastener is at Rockwell C33-C39 hardness. Finally, a finish is applied.