The present invention provides a high strength steel sheet with 780 MPa class tensile strength excellent in bending workability and fatigue strength. The high strength steel sheet is (1) a steel sheet whose steel composition contains: C: 0.05-0.20%; Si: 0.6-2.0%; Mn: 1.6-3.0%; P: 0.05% or below; S: 0.01% or below; Al: 0.1% or below; and N: 0.01% or below, the balance comprising iron and inevitable impurities, in which (2) a microstructure comprises a polygonal ferrite structure and a structure formed by low-temperature transformation, in which, when a sheet plane located at a depth of 0.1 mm from a surface of the steel sheet is in the observation under a scanning electron microscope with respect to twenty sights in total in different positions in the sheet-width direction, the maximum value of the areal proportion of the polygonal ferrite (Fmax) and the minimum value of the areal proportion of the ferrite (Fmin) in a 50 μm×50 μm area in each sight satisfy Fmax≦80%, Fmin≧10%, and Fmax−Fmin≦40%.