Disclosed herein is a high-strength hot-rolled steel sheet which is characterized by high strength (in terms of tensile strength at 900 MPa level) and excellent combined formability expressed by balance between strength and ductility [tensile strength (TS)×total elongation (El)] and balance between strength and stretch flangeability [tensile strength (TS)×bore expanding ratio (λ)]. The hot-rolled steel sheet contains C: no less than 0.02% and no more than 0.15%, Si: no less than 0.2% and no more than 2.0%, Mn: no less than 0.5% and no more than 2.5%, Al: no less than 0.02% and no more than 0.15%, Cu: no less than 1.0% and no more than 3.0%, Ni: no less than 0.5% and no more than 3.0%, and Ti: no less than 0.03% and no more than 0.5%. (% means mass %) It also has a metallographic structure in longitudinal cross section such that the sum of bainitic ferrite and granular bainitic ferrite accounts for no less than 85% by area.