In a method for manufacturing ceramic plates, a Pd paste which does not diffuse into ceramic is formed; metal films each having a thickness such that ceramic layers to be formed after firing are not connected to each other in the lamination direction are formed on surfaces of ceramic green sheets using the Pd paste; then, a firing treatment at a firing temperature, which is a high temperature at which no glass component remains on surfaces of the ceramic layers after the firing and which is equal to or lower than a decomposition temperature of a ceramic material forming the ceramic layers, is performed for a laminate; oxygen present at the interfaces between the ceramic layers and the metal layers is removed by immersing a sintered body in n-butyl alcohol so as to separate the ceramic layers and the metal layers.