The invention relates to a molding mass made from vinyl chloride polymer or polyvinylchloride at 5 to 94 wt. % and a K value of 50 to 90 additives at 2 to 25 wt. % and a polymer, whereby the weight percentages relate to the total weight of the molding mass. The polymer is a semi-crystalline or amorphous polyester. The film is produced from the molding mass by plastifying and fusing the same and calendering or extruding the same to give a film with a thickness of 100 microns to 1 mm. By means of subsequent in-line or off-line method steps, the film, for example, by means of drawing with a drawing degree of 1.3 to 7, can be further processed to give a thin high-shrinkage film.