There are provided a method for measuring strength of a chemically strengthened glass, that reflects the state of actual drop fracture more appropriately, and can reproduce slow cracking in the chemically strengthened glass, a method for reproducing cracking of a chemically strengthened glass, and a method for producing a chemically strengthened glass. Load is applied to an indenter having a tip formed into a sharp shape having a minimum angle θmin of cross-section of less than 120°, the indenter is pushed into a chemically strengthened glass under a static load condition such that the tip is vertical to a surface of the chemically strengthened glass, and the load when the chemically strengthened glass cracks is measured.