A method of making a polymer with stable Mooney viscosity and molecular weight is described. A conjugated diolefin is reacted in a hydrocarbon solvent in the presence of an initiator to form a polymer. After forming the polymer, alkoxy silane terminal functionalizing groups are bonded to the polymer. A mixture of at least one of a first stabilizing agent having the formula (R)4-nSi(OH)n wherein R is a C1 to C18 alkyl, C1 to C18 alkyl group containing a heteroatom such as nitrogen or oxygen, C4 to C8 cycloalkyl, or C6 to C18 aromatic group, and a at least one of a second stabilizing agents having the formula (R)2Si(OH)2 wherein R is an aryl group, is then added to the polymer, optionally in the presence of hydrocarbon oil. The polymer is then desolvatized, resulting in a polymer with stable Mooney viscosity and molecular weight, even over prolonged periods of time. Compositions and articles containing the polymer are also described.