A method comprising a) calcining a silica support at temperature in the range of from about 100° C. to about 500° C. to form a precalcined silica support; b) contacting the precalcined silica support with a titanium alkoxide to form a titanated support; c) subsequent to b), contacting the titanated support with a polyol to form a polyol associated titanated support (PATS); d) contacting at least one of the silica support, pre-calcined silica support, the titanated support, the PATS, or combinations thereof with a chromium-containing compound to form a polymerization catalyst precursor; e) drying the polymerization catalyst precursor to form a dried polymerization catalyst precursor; and f) calcining the dried polymerization catalyst precursor to produce a polymerization catalyst, wherein less than about 0.1 wt. % of a highly reactive volatile organic compound (HRVOC) is emitted during the calcining of the dried polymerization catalyst precursor.