The present invention provides an austenite-ferrite stainless steel. The steel composition contains in % by weight: 0.01%≦C≦0.10% 20.0%≦Cr≦24.0% 1.0%≦Ni≦3.0% 0.12%≦N≦0.20% 0.5%≦Mn≦2.0% 1.6%≦Cu≦3.0% 0.05%≦Mo≦1.0% W≦0.15% 0.05%≦Mo+W/2≦1.0% 0.2%≦Si≦1.5% Al≦0.05% V≦0.5% Nb≦0.5% Ti≦0.5% B≦0.003% Co≦0.5% REM≦0.1% Ca≦0.03% Mg≦0.1% Se≦0.005% O≦0.01% S≦0.030% P≦0.040% the rest being iron and impurities resulting from the production and the microstructure being composed of austenite and 35 to 65% ferrite by volume, the composition furthermore obeying the following relations: 40≦IF≦65 with IF=10% Cr+5.1% Mo+1.4% Mn+24.3% Si+35% Nb+71.5% Ti−595.4% C−245.1% N−9.3% Ni−3.3% Cu−99.8 and IRCGCU≧32.0 with IRCGCU=% Cr+3.3% Mo+2% Cu+16% N+2.6% Ni−0.7% Mn and 0≦IU≦6.0 with IU=3% Ni+% Cu+% Mn−100% C−25% N−2(% Cr+% Si)−6% Mo+45 as well as a method of manufacture of plates, bands, coils, bars, wires, profiles, forged pieces and molded pieces of this steel.