In at least one embodiment, an assembly is provided comprising a first member including a 6xxx series aluminum alloy heat treated to have a yield strength of at least 200 MPa and an r/t (bendability) ratio of up to 0.4. One or more members may be secured to the first member with a rivet (e.g., a self-piercing rivet). The heat treated alloy may have a yield strength of at least 260 MPa and may have a bendability ratio of up to 0.3. A method of forming an assembly is also provided, including heat treating a 6xxx series aluminum alloy to produce an alloy having a yield strength of at least 200 MPa and an r/t (bendability) ratio of up to 0.4 and riveting a member including the heat treated alloy to one or more additional members.