The present invention provides an aluminum alloy foil for electrode current collector, high in strength and superior in heat resistance after the active material coating/drying process of the manufacture of the battery, a manufacturing method thereof, and a lithium ion secondary battery. According to the present invention, an aluminum alloy foil for electrode current collector, including 0.1 to 0.5 mass % (hereinafter mass % is referred to as %) of Fe, 0.01 to 0.5% of Si, 0.01 to 0.2% of Cu, 0.01 to 0.5% of Mn, with the rest being Al and unavoidable impurities, wherein tensile strength of an aluminum alloy foil and a heat treatment selected from 24 hours at 100° C., 3 hours at 150° C., and 15 minutes at 200° C., is 210 MPa or higher, a manufacturing method thereof, and a lithium ion secondary battery are provided.