公开(公告)号：KR1020140048443A
公开(公告)日：2014-04-24
申请号：KR1020120114080
申请日：2012-10-15
Applicant: 강릉원주대학교산학협력단
IPC: C01G23/053 , B82B3/00
Abstract: Provided is a method of fabricating a nanostructure of titanium dioxide to enable cost-efficient and safe mass-production through a simple process. The method of fabricating a nanostructure of titanium dioxide comprises: a step of providing an aqueous solution containing titanium dioxide and potassium hydroxide; a step of forming titanium dioxide nanoparticles by irradiating the aqueous solution with microwaves. [Reference numerals] (S100) Provide an aqueous solution containing titanium dioxide and potassium hydroxide; (S200) Form titanium dioxide nanoparticles by irradiating the aqueous solution with microwaves
Abstract translation: 提供了一种制造二氧化钛纳米结构的方法，以通过简单的工艺实现经济高效和安全的批量生产。 制备二氧化钛纳米结构的方法包括：提供含有二氧化钛和氢氧化钾的水溶液的步骤; 通过用微波照射水溶液来形成二氧化钛纳米颗粒的步骤。 （附图标记）（S100）提供含有二氧化钛和氢氧化钾的水溶液; （S200）通过用微波照射水溶液来形成二氧化钛纳米颗粒
-
公开(公告)号：KR101851879B1
公开(公告)日：2018-04-24
申请号：KR1020160181830
申请日：2016-12-29
Applicant: 강릉원주대학교산학협력단
IPC: C01B32/956 , C04B35/565 , C04B35/64 , C04B35/626 , C04B35/63
CPC classification number: C01B32/956 , C01P2006/80 , C04B35/565 , C04B35/62615 , C04B35/63 , C04B35/64 , C04B2235/424 , C04B2235/425 , C04B2235/428 , C04B2235/445 , C04B2235/666
Abstract: 본발명은고순도탄화규소의제조방법에관한것이다. 본발명에따른탄화규소의제조방법은불화마그네슘을포함하는소결조제를이용하여아크방전을수행함으로써, 반응온도가반응물외부로분산되는것을차단하여탄화규소의생성속도를향상시킬수 있을뿐만아니라, 부반응을억제하여탄화규소의제조효율및 순도를향상시키는효과가우수하다.
-
公开(公告)号：KR101540535B1
公开(公告)日：2015-08-03
申请号：KR1020140014265
申请日：2014-02-07
Applicant: 강릉원주대학교산학협력단
Abstract: 본발명은용매에철 질산염및 이산화규소를혼합하여슬러리를제조하는단계; 상기단계에서제조된슬러리를건조한후 분쇄하는단계; 및상기단계에서분쇄된분말을전기로에서가열하는단계를포함하는페로실리콘의제조방법에관한것이다.
Abstract translation: 本发明涉及一种制造硅铁的方法，包括：通过将硝酸铁和二氧化硅与溶剂混合来制备浆料的步骤; 干燥由上述工序制造的浆料后的研磨工序; 以及在电炉中在上述步骤中加热粉末研磨的步骤。
-
公开(公告)号：KR101437826B1
公开(公告)日：2014-09-15
申请号：KR1020120111301
申请日：2012-10-08
Applicant: 강릉원주대학교산학협력단
CPC classification number: C03B19/08 , B09B3/00 , C03C11/007
Abstract: 본 발명은, 폐유리를 이용하여 유리의 용융이나 가수분해 또는 그 외의 사전 공정을 요구하지 않고, 단순한 공정을 이용하여 저밀도를 가지고 균일한 기공 분포를 가지는 발포 유리 제조 방법을 제공한다. 본 발명의 일실시예에 따른 발포 유리 제조 방법은, 폐유리를 준비하는 단계; 상기 폐유리에 서로 화학반응하여 기포를 형성하는 기포 형성제와 산소 공급제를 첨가하고, 상기 폐유리를 분쇄하여 유리 분쇄물을 형성하는 단계; 상기 유리 분쇄물을 성형하여 유리 성형물을 형성하는 단계; 및 상기 유리 성형물을 열처리하여 기포를 포함하는 발포 유리를 형성하는 단계;를 포함한다.
-
Patent Agency Ranking
公开(公告)号：KR1020170054042A
公开(公告)日：2017-05-17
申请号：KR1020150156724
申请日：2015-11-09
Applicant: 강릉원주대학교산학협력단
Abstract: 본발명은고순도탄화규소(SiC)의제조방법에관한것이다. 본발명에따른탄화규소(SiC)의제조방법은불화칼슘(CaF)을포함하는소결조제를이용하여아크방전을수행함으로써반응온도가반응물외부로분산되는것을차단하여탄화규소(SiC)의생성속도를향상시킬수 있을뿐만아니라부반응을억제하여탄화규소의제조효율및 순도를향상시키는효과가우수하다.
Abstract translation: 本发明涉及生产高纯度碳化硅（SiC）的方法。 根据本发明的用于制造碳化硅（SiC）的方法包括使用含有氟化钙（CaF）的烧结助剂来执行电弧放电，以防止反应温度分散在反应物之外， 而且通过抑制副反应来提高碳化硅的生产效率和纯度的效果也是优异的。
-
公开(公告)号：KR101445549B1
公开(公告)日：2014-10-01
申请号：KR1020120114080
申请日：2012-10-15
Applicant: 강릉원주대학교산학협력단
IPC: C01G23/053 , B82B3/00
Abstract: 본 발명은 단순한 공정으로 경제적이고 안전하게 대량생산할 수 있는 이산화티타늄 나노구조체의 제조방법을 구현하기 위하여, 이산화티타늄 및 수산화칼륨을 포함하는 수용액을 제공하는 단계; 및 상기 수용액에 마이크로웨이브를 조사하여 이산화티타늄 나노결정을 형성하는 단계;를 구비하는, 이산화티타늄 나노구조체의 제조방법이 제공된다.
-
公开(公告)号：KR1020140048361A
公开(公告)日：2014-04-24
申请号：KR1020120111301
申请日：2012-10-08
Applicant: 강릉원주대학교산학협력단
CPC classification number: C03B19/08 , B09B3/00 , C03C11/007
Abstract: The present invention provides a method for manufacturing a foamed glass that has low density and uniform pore distribution by using a waste glass in a simple process without a melting of glass, hydrolysis, or other pre-processes. The method for manufacturing the foamed glass according to an embodiment of the present invention includes a step of preparing the waste glass; a step of adding a bubble forming agent for forming bubbles on the waste glass through a chemical reaction and an oxygen supply agent and forming a pulverized glass by pulverizing the waste glass; a step of forming a molded glass by molding the pulverized glass; and a step of forming the foamed glass including bubbles by heating the molded glass. [Reference numerals] (S10) Preparing waste glass; (S20) Forming a first pulverized glass by firstly pulverizing the waste glass; (S30) Adding a chemical reaction and an oxygen supply agent in the first pulverized glass; (S40) Forming a second pulverized glass by secondly pulverizing the first pulverized glass in which the chemical reaction and the oxygen supply agent are added; (S50) Drying the second pulverized glass; (S60) Molding the dried second pulverized glass; (S70) Forming a glass molding material by molding the second pulverized glass; (S80) Forming a foamed glass by heating the molded glass
Abstract translation: 本发明提供一种制造泡沫玻璃的方法，该方法通过在没有玻璃熔融，水解或其它预处理的简单方法中使用废玻璃而具有低密度和均匀的孔分布。 根据本发明的实施方案的制造泡沫玻璃的方法包括制备废玻璃的步骤; 通过化学反应和氧供给剂在废玻璃上添加用于形成气泡的气泡形成剂并通过粉碎废玻璃形成粉碎玻璃的步骤; 通过模制所述粉碎玻璃来形成模制玻璃的步骤; 以及通过加热模制玻璃来形成包括气泡的泡沫玻璃的步骤。 （附图标记）（S10）准备废玻璃; （S20）首先将废玻璃粉碎形成第一粉碎玻璃; （S30）在第一粉碎玻璃中添加化学反应和氧供给剂; （S40）通过二次粉碎添加有化学反应和供氧剂的第一粉碎玻璃来形成第二粉碎玻璃; （S50）干燥第二粉碎玻璃; （S60）将干燥的第二粉碎玻璃成型; （S70）通过模制第二粉碎玻璃形成玻璃成型材料; （S80）通过加热成型玻璃形成发泡玻璃
-
-
公开(公告)号：KR101589835B1
公开(公告)日：2016-01-29
申请号：KR1020140180644
申请日：2014-12-15
Applicant: 강릉원주대학교산학협력단
Abstract: 본발명은, 망간질산염및 이산화규소를사용하여제조함으로써, 공정시간및 비용을최소화하며, 실리콘회수율이향상되는효과가있는실리콘-망간합금및 이의제조방법에관한것이다.
Abstract translation: 硅锰合金及其制备方法技术领域本发明涉及一种硅锰合金及其制备方法。 本发明使用硝酸锰和二氧化硅制造，以便最小化处理时间和成本并提高硅回收率。 根据硅锰合金，硅含量（Si）与锰（Mn）的重量比满足38-45:55-62。
-
-
-
-
-
-
-
-