公开(公告)号：KR1020130131003A
公开(公告)日：2013-12-03
申请号：KR1020120054715
申请日：2012-05-23
Applicant: 전남대학교산학협력단
Abstract: The present invention relates to a graphite nanofiber and a production method thereof. The production method of the graphite nanofiber comprises the steps of: mixing a carbon fiber precursor material and a solvent to obtain a mixed solution; adding a metal precursor and homogenizing the mixed solution; adding silicon oxide and homogenizing the mixed solution; producing fibers by electrospinning the homogenized mixed solution; and thermally treating the produced fibers. The graphite nanofiber produced by the method has a structure where graphite sheets are vertically arranged with respect to the nanofiber axis, and contains graphene, catalyst metal particles, and silicon compounds to be used for an electrode material of a solar cell or a secondary battery. [Reference numerals] (AA) Start;(BB) End;(S11) Mix a carbon fiber precursor material and a solvent to obtain a mixed solution;(S12) Add a metal precursor and firstly homogenize the mixed solution;(S13) Add silicon oxide and secondly homogenize the mixed solution;(S14) Produce fibers by electrospinning the homogenized mixed solution;(S15) Thermally treat the fibers;(S16) Obtain graphene-containing graphite nanofibers
Abstract translation: 石墨纳米纤维及其制造方法技术领域本发明涉及石墨纳米纤维及其制造方法。 石墨纳米纤维的制造方法包括以下步骤：将碳纤维前体材料和溶剂混合以获得混合溶液; 加入金属前体并均化混合溶液; 加入氧化硅并均化混合溶液; 通过电纺均匀混合溶液生产纤维; 并对所生产的纤维进行热处理。 通过该方法制造的石墨纳米纤维具有石墨片相对于纳米纤维轴垂直布置的结构，并且包含用于太阳能电池或二次电池的电极材料的石墨烯，催化剂金属颗粒和硅化合物。 （AA）开始（BB）结束;（S11）将碳纤维前体材料和溶剂混合，得到混合溶液;（S12）添加金属前体，首先使混合溶液均化;（S13）添加 氧化硅，二次均化混合溶液;（S14）静电纺丝均质混合液生产纤维;（S15）热处理纤维;（S16）获得含石墨烯的石墨纳米纤维
-
Patent Agency Ranking
公开(公告)号：KR101407236B1
公开(公告)日：2014-06-13
申请号：KR1020120054715
申请日：2012-05-23
Applicant: 전남대학교산학협력단
Abstract: 본 발명은 흑연나노섬유 및 그 제조방법에 관한 것이다. 본 발명에 따른 흑연나노섬유의 제조방법은, 탄소섬유 전구체 물질 및 용매를 혼합하여 혼합용액을 제조하는 단계와; 금속 전구체를 첨가하여 상기 혼합용액을 균질화하는 단계와; 실리콘산화물을 첨가하여 상기 혼합용액을 균질화하는 단계와; 상기 균질화된 혼합용액을 전기방사하여 섬유를 제조하는 단계와; 상기 제조된 섬유를 열처리하는 단계를 포함한다. 이에 의해 제조된 흑연나노섬유는, 흑연시트들이 나노섬유 축에 대하여 수직방향으로 배열되어 있는 구조를 가지고, 그래핀, 촉매 금속 입자 및 실리콘 화합물을 포함하고 있어, 태양전지 또는 이차전지용 전극물질로 유용하게 이용될 수 있다.
-
公开(公告)号：KR101370868B1
公开(公告)日：2014-03-27
申请号：KR1020120037520
申请日：2012-04-10
Applicant: 전남대학교산학협력단 , 주식회사 포스포
Abstract: 본 발명은 폴리퍼퓨릴 알콜을 이용한 탄소섬유 및 이의 제조방법을 제공하는 것으로, 본 발명의 탄소섬유는 기존 음극물질인 흑연에 비해 비용량을 획기적으로 높일 수 있으며, 특히 폴리아크릴로나이트릴을 단독으로 이용한 탄소섬유에 비해 기계적 물성, 초기비가역용량 및 사이클 특성을 향상시킬 수 있다. 또한 폴리퍼퓨릴 알콜을 이용한 탄소섬유는 염료감응 태양전지용 상대전극으로써 매우 높은 광전환효율을 나타낸다.
-
公开(公告)号：KR1020120115960A
公开(公告)日：2012-10-19
申请号：KR1020120037520
申请日：2012-04-10
Applicant: 전남대학교산학협력단 , 주식회사 포스포
CPC classification number: D01F9/14 , D01D1/02 , D01D5/0007 , D01D10/02 , D01F9/22 , H01M4/02 , H01M4/9083
Abstract: PURPOSE: A carbon fiber using polyacene-based compounds and a method for fabricating the same are provided to improve coulombic efficiency at first cycle and to obtain the carbon fiber with excellent cycle stability. CONSTITUTION: A method for fabricating a carbon fiber comprises: a step of electrospinning a spinning composition containing polyacene-based compounds and carbon precursor at 20-30kV of voltage and preparing fiber type precursor; a step of performing thermal treatment of the precursor at 220-300 Deg. C.; and a step of carbonizing the precursor at 300-3000 Deg. C.The polyacene-based compounds includes 3,4,9,10-perylene tetra carboxylic hydride, polyacene, polyacenoacene, polyacethylene, polystylene, phenol, polyphenylene sulfide, poly-paraphenylene, or pitch. The spinning composition further contains a metal precursor.
Abstract translation: 目的：提供使用多并苯类化合物的碳纤维及其制造方法，以提高第一次循环的库仑效率，得到优异的循环稳定性的碳纤维。 构成：制造碳纤维的方法包括：在20-30kV的电压下静电纺丝含有多并苯类化合物和碳前体的纺丝组合物并制备纤维型前体的步骤; 在220-300度下进行前体的热处理的步骤。 C。; 以及在300-3000度碳酸化前体的步骤。 多并苯类化合物包括3,4,9,10-苝四羧酸氢化物，多并苯，聚并三烯，聚亚乙基，聚苯乙烯，苯酚，聚苯硫醚，聚对亚苯基或沥青。 纺丝组合物还含有金属前体。
-
公开(公告)号：KR101370867B1
公开(公告)日：2014-03-31
申请号：KR1020120037517
申请日：2012-04-10
Applicant: 전남대학교산학협력단 , 주식회사 포스포
Abstract: 본 발명은 폴리아센계 화합물을 이용한 탄소섬유 및 그의 제조방법에 관한 것으로, 폴리아센계 화합물과 탄소 전구체의 혼합용액을 전기방사, 산화 안정화 및 탄화하여 제조된 이차전지의 음극으로 사용할 경우 용량이 매우 커지고, 첫 사이클에서 개선된 쿨롱 효율을 보일 뿐만 아니라, 동시에 사이클 안정성이 매우 우수하다.
-
公开(公告)号：KR1020120115959A
公开(公告)日：2012-10-19
申请号：KR1020120037517
申请日：2012-04-10
Applicant: 전남대학교산학협력단 , 주식회사 포스포
Abstract: PURPOSE: A carbon fiber using polyacene-based compounds and a method for fabricating the same are provided to remarkably improve specific capacity and initial irreversible capacity. CONSTITUTION: A method for fabricating carbon fibers comprises: a step of electrospinning a spinning composition containing polyacene compounds and carbon precursor and prepare a fiber type precursor; a step of performing the precursor under the presence of oxydation-stabilized fiber type precursor; and a step of carbonizing the precursor and obtaining the carbon fibers. The spinning composition further contains a metal precursor including copper(Cu), nickel(Ni), cobalt(Co), tin(Sn), silicon(Si), iron(Fe), antimony(Sb), aluminum(Al), or bismuth(Bi).
Abstract translation: 目的：提供使用多并苯类化合物的碳纤维及其制造方法，以显着提高比容量和初始不可逆容量。 构成：制造碳纤维的方法包括：将含有多并苯化合物和碳前体的纺丝组合物静电纺丝并制备纤维型前体的步骤; 在氧化稳定的纤维型前体存在下进行前体的步骤; 以及将前体碳化并获得碳纤维的步骤。 纺丝组合物还含有包含铜（Cu），镍（Ni），钴（Co），锡（Sn），硅（Si），铁（Fe），锑（Sb），铝（Al） 铋（Bi）。
-
-
-
-
-