公开(公告)号：KR1020100076672A
公开(公告)日：2010-07-06
申请号：KR1020080134797
申请日：2008-12-26
Applicant: 전자부품연구원
CPC classification number: C01B32/16 , B82B3/0004 , C01B32/225 , C01B32/342
Abstract: PURPOSE: A method for manufacturing a carbon rod for synthesizing a carbon nanotube is provided to inexpensively manufacture the carbon nanotube with a carbon rod made of expanded graphite, and to uniform quality of the carbon nanotube. CONSTITUTION: A method for manufacturing a carbon rod for synthesizing a carbon nanotube includes the following steps: preparing expanded graphite containing sulfuric acid and nitric acid(S110); producing the expanded graphite by heat-treating the expanded graphite in the air(S120); gaining a solid or a liquid mixture by mixing graphite and catalyst particles(S130); and completing the carbon rod by molding and compressing the solid or the liquid mixture(S140). The catalyst particles contain Fe, Ni, Co, FeS, NiS, CoS or a mixture of other materials.
Abstract translation: 目的：提供一种碳纳米管合成碳棒的制造方法，由碳纳米管制成碳纳米管，碳棒由膨胀石墨制成，质量均匀。 构成：用于制造碳纳米管的碳棒的制造方法包括以下步骤：制备含有硫酸和硝酸的膨胀石墨（S110）; 通过对空气中的膨胀石墨进行热处理来生产膨胀石墨（S120）; 通过混合石墨和催化剂颗粒获得固体或液体混合物（S130）; 并通过模制和压缩固体或液体混合物来完成碳棒（S140）。 催化剂颗粒含有Fe，Ni，Co，FeS，NiS，CoS或其他材料的混合物。
-
2.发明授权잉여 분산제 제거를 통한 수분산 탄소나노튜브 용액의 순도 향상 방법 및 그 방법으로 제조된 수분산 탄소나노튜브 용액 失效通过去除多余的分散剂和水分散的碳纳米管涂层溶液，分散碳纳米管溶液的纯度升高方法
公开(公告)号：KR101082115B1
公开(公告)日：2011-11-10
申请号：KR1020090040678
申请日：2009-05-11
Applicant: 전자부품연구원
Abstract: 본발명은잉여분산제제거를통한수분산탄소나노튜브(carbon nanotube; CNT) 용액의순도향상방법및 그방법으로제조된수분산탄소나노튜브용액에관한것으로, 원소재수분산탄소나노튜브용액에포함되어있는잉여분산제제거를통하여수분산탄소나노튜브용액의순도를향상시키기위한것이다. 본발명에따르면, 잉여분산제가포함된원소재수분산탄소나노튜브용액과유기용매를혼합하여혼합액을형성하고, 혼합액을와동시켜잉여분산제를콜로이드입자로형성시키고, 일정시간경과후 수분산탄소나노튜브용액과유기용매가상 분리되어잉여분산제콜로이드입자가유기용매로추출되면, 유기용매에대해서상 분리된수분산탄소나노튜브용액을분리한다.
-
Patent Agency Ranking
公开(公告)号：KR101008216B1
公开(公告)日：2011-01-17
申请号：KR1020080134880
申请日：2008-12-26
Applicant: 전자부품연구원
Abstract: 본 발명은, 용액 상태에서 고분자 물질 내에 탄소나노튜브를 균일하게 나노 분산시키고, 극성이 다른 특정 용매를 사용함으로써 탄소나노튜브와 고분자 물질과의 혼합물을 상 분리에 의해 순간 침전시켜, 우수한 분산 상태를 나타내는 탄소나노튜브-폴리카보네이트 컴파운드 제조 방법에 관한 것이다.
본 발명에 따른 탄소나노튜브-폴리카보네이트 컴파운드 제조 방법은 탄소나노튜브-폴리카보네이트 용액을 제공하는 단계; 아세톤 수용액을 제공하는 단계; 상기 탄소나노튜브-폴리카보네이트 용액에 상기 아세톤 수용액을 첨가하여 침전물을 생성하는 단계; 및 생성된 상기 침전물을 분리하는 단계를 포함하는 것을 구성적 특징으로 한다.
탄소나노튜브, 폴리카보네이트 화합물-
公开(公告)号：KR1020100076742A
公开(公告)日：2010-07-06
申请号：KR1020080134880
申请日：2008-12-26
Applicant: 전자부품연구원
CPC classification number: C08K3/04 , B82Y30/00 , C08J3/14 , C08J3/28 , C08K9/04 , C08K2201/001 , C08K2201/011 , C08L69/00
Abstract: PURPOSE: A producing method of a carbon nanotube-polycarbonate compound is provided to produce a compound in which a carbon nanotube is uniformly dispersed in a polymer matrix, and to reduce the producing cost. CONSTITUTION: A producing method of a carbon nanotube-polycarbonate compound comprises the following steps: producing a carbon nanotube-polycarbonate solution(S100); providing an acetone solution(S200); producing a precipitate by adding the acetone solution to the nanotube-polycarbonate solution(S300); and separating the precipitate(S400). The mixture ratio of distilled water and acetone of the acetone solution is 1.2:0.8. The producing method additionally comprises a step of drying the precipitate for 24 hours at the temperature over 60 deg C.
Abstract translation: 目的：提供碳纳米管 - 聚碳酸酯化合物的制造方法，制造碳纳米管均匀地分散在聚合物基质中的化合物，降低制造成本。 构成：碳纳米管 - 聚碳酸酯化合物的制造方法包括以下步骤：制备碳纳米管 - 聚碳酸酯溶液（S100）; 提供丙酮溶液（S200）; 通过向纳米管 - 聚碳酸酯溶液中加入丙酮溶液（S300）产生沉淀物; 并分离沉淀物（S400）。 丙酮溶液的蒸馏水和丙酮的混合比为1.2:0.8。 该制备方法还包括在60℃以上的温度下干燥沉淀24小时的步骤。
-
5.发明公开잉여 분산제 제거를 통한 수분산 탄소나노튜브 용액의 순도 향상 방법 및 그 방법으로 제조된 수분산 탄소나노튜브 용액 失效通过移除喷雾剂和水分散的碳纳米管涂层溶液来分散碳纳米管溶液的净化方法
公开(公告)号：KR1020100121804A
公开(公告)日：2010-11-19
申请号：KR1020090040678
申请日：2009-05-11
Applicant: 전자부품연구원
CPC classification number: C01B32/17 , B82B3/00 , C01B32/174 , C01B2202/28
Abstract: PURPOSE: A purity improvement method of a water-dispersed carbon nanotube solution, and the water-dispersed carbon nanotube solution manufactured therefrom are provided to use an organic solvent for selectively remove a surplus dispersing agent. CONSTITUTION: A purity improvement method of a water-dispersed carbon nanotube solution comprises the following steps: mixing a raw material water-dispersible carbon nanotube solution(10) containing a surplus dispersing agent(18), with an organic solvent(20) to form a mixed solution; rotating the mixed solution to form a colloid particle with the surplus dispersing agent around a particle of the raw material water-dispersible carbon nanotube solution; phase separating the water-dispersible carbon nanotube solution(10a) from the organic solvent, for extracting the colloid particle; and separating the water-dispersible carbon nanotube solution.
Abstract translation: 目的：提供水分散碳纳米管溶液的纯度改善方法和由其制备的水分散碳纳米管溶液，以使用有机溶剂选择性除去多余的分散剂。 构成：水分散碳纳米管溶液的纯度改善方法包括以下步骤：将含有多余分散剂（18）的原料水分散性碳纳米管溶液（10）与有机溶剂（20）混合以形成 混合溶液; 旋转混合溶液以形成具有多余分散剂的胶体颗粒在原料水分散性碳纳米管溶液的颗粒周围; 将水分散性碳纳米管溶液（10a）从有机溶剂中分离，萃取胶体粒子; 并分离水分散性碳纳米管溶液。
-
公开(公告)号：KR101060515B1
公开(公告)日：2011-08-30
申请号：KR1020080134797
申请日：2008-12-26
Applicant: 전자부품연구원
Abstract: 본 발명은 전기 방전법에 의한 탄소나노튜브를 합성하기 위해 사용되는 탄소봉을 팽창 흑연재료를 이용하여 제작하는 방법에 관한 것이다.
본 발명에 따르는 탄소나노튜브 합성용 탄소봉은 (i) 흑연층 사이에 황산 및 질산 중의 적어도 하나가 함유된 가팽창 흑연을 준비하는 단계; (ii) 상기 가팽창 흑연을 공기 분위기에서 열처리하여 팽창 흑연을 생성하는 단계; (iii) 상기 생성된 팽창 흑연과 촉매 입자를 고상 또는 액상 혼합하여 고상 또는 액상 혼합물을 얻는 단계; 및 (iv) 상기 고상 또는 액상 혼합물을 압축 성형하여 탄소나노튜브 합성용 탄소봉을 완성하는 단계에 의해 구성되는 것을 특징으로 한다.
탄소봉, 탄소나노튜브, 팽창 흑연-
公开(公告)号：KR1020100134479A
公开(公告)日：2010-12-23
申请号：KR1020090053114
申请日：2009-06-15
Applicant: 전자부품연구원 , 재단법인 한국탄소융합기술원
CPC classification number: B82B3/0009 , B82B3/0061 , C01B32/158
Abstract: PURPOSE: A method for preparing CNT powder coated with metal nanoparticles is provided to ensure high dispersibility and bondability by applying metal to the surface of a carbon nanotube with affinity and density similar to metal used for a carbon nanotube/metal complex. CONSTITUTION: A method for preparing CNT powder coated with metal nanoparticles comprises the steps of: treating a carbon nanotube with a strong acid; mixing the carbon nanotube treated with a strong acid with metal acetylacetonate solution; filtering the carbon nanotube/metal acetylacetonate mixture and drying it to obtain carbon nanotube/metal acetylacetonate powder; and heating the carbon nanotube/metal acetylacetonate powder in a reactor of a non-oxidizing atmosphere, decomposing the metal acetylacetonate, and coating the surface of the carbon nanotube with the metal nanoparticles.
Abstract translation: 目的：提供一种制备涂覆有金属纳米颗粒的CNT粉末的方法，通过将金属与碳纳米管/金属络合物所用金属的亲和性和密度相似，将金属施加到碳纳米管表面，确保高分散性和粘合性。 构成：用金属纳米颗粒制备CNT粉末的方法包括以下步骤：用强酸处理碳纳米管; 将用强酸处理的碳纳米管与金属乙酰丙酮溶液混合; 过滤碳纳米管/金属乙酰丙酮化物混合物并干燥得到碳纳米管/金属乙酰丙酮化物粉末; 并在非氧化性气氛的反应器中加热碳纳米管/金属乙酰丙酮粉末，分解金属乙酰丙酮化物，并用金属纳米粒子涂覆碳纳米管表面。
-
-
-
-
-
-