公开(公告)号：KR1020090066881A
公开(公告)日：2009-06-24
申请号：KR1020070134617
申请日：2007-12-20
Applicant: 주식회사 포스코 , 재단법인 포항산업과학연구원
Abstract: An electrode material for electric double-layer capacitor and a manufacturing method thereof are provided to reduce a manufacturing cost and an environmental load by reducing largely consumption of cleaning water and generation of waste water. A first impurity removal process is performed to remove impurities by using an alkali solution of 0.1mol/L to saturation concentration. A second impurity removal process is performed to remove the impurities by processing activated carbon by using an acid solution of 0.1mol/L to saturation concentration. A cleaning and drying process is performed by using water and air. A heat treatment process is performed at the temperature of 300 to 1200 degrees centigrade during 5 minutes to 10 hours in an inactive atmosphere or reductive atmosphere.
Abstract translation: 提供一种双电层电容器用电极及其制造方法，其通过减少大量的清洗水的消耗和废水的产生来降低制造成本和环境负荷。 通过使用0.1mol / L的碱溶液至饱和浓度来进行第一杂质去除过程以除去杂质。 通过使用0.1mol / L的酸溶液至饱和浓度来处理活性炭来进行第二杂质去除处理以除去杂质。 清洁和干燥过程通过使用水和空气进行。 在惰性气氛或还原气氛中，在300〜1200摄氏度的温度下进行5分钟〜10小时的热处理。
-
公开(公告)号：KR100613259B1
公开(公告)日：2006-09-25
申请号：KR1020020083068
申请日：2002-12-24
Applicant: 재단법인 포항산업과학연구원
Abstract: 본 발명은 ZrO
2 -C계 내화물 조성물에 관한 것으로서, 상기 조성물은 ZrO
2 클링커 70 내지 85 중량% 및 인상흑연 15 내지 30 중량%의 혼합물 100 중량부; 액상 페놀수지 2 내지 4 중량부; 및 연화점이 100 내지 250℃인 석탄계 또는 석유계 고상 핏치 1 내지 5 중량부를 포함한다.
연화점, 고상 핏치, 내화물-
公开(公告)号：KR1020060071526A
公开(公告)日：2006-06-27
申请号：KR1020040110139
申请日：2004-12-22
Applicant: 재단법인 포항산업과학연구원
Inventor： 박세민
Abstract: 본 발명은 탄소계 내화물 조성물에 관한 것으로, 특히 산화물 골재, 카본 블랙, 섬유상 탄소 재료, 결합재, 및 산화방지제를 포함하여 종래 내화물과 비교하여 내스폴링성이 우수하고, 강도가 현저히 향상된 탄소계 내화물 조성물에 관한 것이다.
탄소계 내화물, 카본블랙, 섬유상 탄소 재료, 내스폴링성, 강도-
公开(公告)号：KR100503353B1
公开(公告)日：2005-07-26
申请号：KR1020020083070
申请日：2002-12-24
Applicant: 재단법인 포항산업과학연구원
Abstract: 본 발명은 MgO-탄소계 내화물 조성물에 관한 것으로, 이 내화물 조성물은 MgO 클린커 100 중량부, 인상흑연 10 내지 20 중량부, 레졸 타입의 액상 페놀 수지 결합재 2 내지 3 중량, 고상 결합재 및 질산 알루미늄 1 내지 5 중량부을 포함한다.
상술한 바와 같이, 본 발명은 질산 알루미늄을 MgO-탄소계 내화물 제조시 첨가함으로써, 내화물의 강도 및 내산화성을 크게 향상시킬 수 있으며, 고상 페놀수지 결합재를 저가의 석탄계/석유계 핏치로 대체하고, 질산 알루미늄을 동시에 첨가함으로써 내화물의 강도 및 내산화성을 크게 향상시킬 수 있다.-
公开(公告)号：KR1020050064539A
公开(公告)日：2005-06-29
申请号：KR1020030096003
申请日：2003-12-24
Applicant: 재단법인 포항산업과학연구원 , (주)카보닉스
IPC: C01B31/04
CPC classification number: C01B32/225 , C01P2004/61
Abstract: 본 발명은 표면처리 흑연으로부터의 팽창흑연 제조방법에 관한 것으로, 기존의 팽창흑연에 도메인(domain)이 형성되고, 미반응 흑연도 다량 관찰되는 등의 반응성에 대한 문제점을 해결하기 위한 것이다.
이를 위하여 본 발명은 천연 혹은 인조 흑연으로부터 팽창흑연을 제조하는 방법에 있어서, 상기 원료 흑연의 표면에 산 또는 산화제 처리시 반응의 활성거점으로 작용할 수 있는 물리적 결함을 부여하는 제 1공정; 상기 표면 결함이 부여된 원료 흑연에 산 또는 산화제 처리를 행하여 팽창흑연을 제조하는 제 2공정으로 이루어지는 팽창흑연 제조방법을 제공하여, 산처리 전의 흑연 원료에 볼밀(ball mill), 제트밀(jet mill) 등을 이용한 밀링(milling) 가공에 의해서 물리적 결함을 부여하여 산 및 산화제와의 화학적 친화성을 개선하는 방법을 통해 팽창흑연 내의 품질 편차를 가능한 줄이고 미반응 흑연의 양을 획기적으로 줄일 수 있도록 한다.-
Patent Agency Ranking
公开(公告)号：KR1020050064061A
公开(公告)日：2005-06-29
申请号：KR1020030095333
申请日：2003-12-23
Applicant: 재단법인 포항산업과학연구원 , (주)카보닉스
IPC: H01M4/04
Abstract: 개시된 발명은 리튬이온전지용 음극재 제조방법에 관한 것으로, 구리 또는 은이 균일하게 분포된 탄소 재료를 제조하기 위한 것이다.
이를 위하여 본 발명은 리튬이온전지용 음극재의 제조방법에 있어서 흑연의 표면에 비정질탄소를 균일하게 피복하는데 있어서 비정질탄소로서 구리 또는 은을 함유한 유기금속화합물을 유기용제에 용해시킨 용액과 비정질탄소 피복재 원료물질을 유기용제에 용해시킨 용액을 혼합한 용액을 1∼30㎛인 흑연분말의 표면에 피복하고 건조한 다음, 불활성 분위기하에서 500∼2000℃의 온도로 탄화시키는 공정에 에 의하는 탄소재료의 제조방법을 제공하여, 본 발명에 의한 탄소재료를 음극재로 사용한 리튬이온전지는 구리 또는 은이 탄소질에 균일하게 분포됨에 의하여 전도성이 우수하므로 싸이클 특성이 우수하며 또한 충방전 용량이 증가하는 효과를 갖는다.-
公开(公告)号：KR1020040056568A
公开(公告)日：2004-07-01
申请号：KR1020020083070
申请日：2002-12-24
Applicant: 재단법인 포항산업과학연구원
CPC classification number: C04B35/66 , C04B35/04 , C04B35/522 , C04B35/6303 , C04B2235/443
Abstract: PURPOSE: Provided is an MgO-carbon-based refractory composition excellent in strength and antioxidation and having high carbonization yield, which contains aluminum nitrate(Al(NO3)3). CONSTITUTION: The MgO-carbon-based refractory composition contains: 100pts.wt. of an MgO clinker; 10-20pts.wt. of a flake graphite; 2-3pts.wt. of a resol type liquid phase phenol resin binder; 1-2pts.wt.(based on the MgO clinker of 100pts.wt.) of a novolac type solid phase phenol resin or 1-5pts.wt.(based on the MgO clinker of 100pts.wt.) of a charcoal- or petroleum-based solid phase pitch powder as a solid phase binder; and 1-5pts.wt. of the aluminum nitrate.
Abstract translation: 目的：提供强度和抗氧化性优异且碳酸化收率高的含有硝酸铝（Al（NO 3）3）的MgO-碳系耐火材料组合物。 构成：MgO-碳基耐火材料组合物含有：100pts.wt。 的MgO熟料; 10-20pts.wt。 片状石墨; 2-3pts.wt。 的甲阶型液相酚醛树脂粘合剂; （基于100ps重量的MgO熟料），酚醛清漆型固相酚醛树脂或1-5pts.wt。（基于100g熟料，100pts.wt。）的木炭或 石油基固相沥青粉作为固相粘合剂; 和1-5pts.wt。 的硝酸铝。
-
公开(公告)号：KR1020040056566A
公开(公告)日：2004-07-01
申请号：KR1020020083068
申请日：2002-12-24
Applicant: 재단법인 포항산업과학연구원
CPC classification number: C04B35/48 , C04B35/522 , C04B35/63496 , C04B2235/443 , C04B2235/448
Abstract: PURPOSE: Provided is a zirconia(ZrO2)-carbon(C)-based refractory composition improving high temperature property and corrosion resistance, which can reduce the cost. CONSTITUTION: The ZrO2-C-based refractory composition comprises: 100pts.wt. of a mixture comprising 70-85wt% of a ZrO2 clinker and 15-30wt% of a flake graphite; 2-4pts.wt. of a liquid phase phenol resin; 1-5pts.wt. of a charcoal- or petroleum-based solid phase pitch having a softening point of 100-250deg.C; additionally, 1-10pts.wt. of an aluminum metal salt.
Abstract translation: 目的：提供改善耐高温性和耐腐蚀性的氧化锆（ZrO 2） - 碳（C）基耐火材料组合物，可降低成本。 构成：基于ZrO2-C的耐火材料组合物包括：100pts.wt。 的混合物，其包含70-85重量％的ZrO 2熟料和15-30重量％的片状石墨; 2-4pts.wt。 的液相酚醛树脂; 1-5pts.wt。 具有软化点为100-250℃的木炭或石油基固相沥青; 另外，1-10pts.wt。 的铝金属盐。
-
公开(公告)号：KR1020030008842A
公开(公告)日：2003-01-29
申请号：KR1020010043840
申请日：2001-07-20
Applicant: 재단법인 포항산업과학연구원
Inventor： 박세민
IPC: B01J23/755 , B82Y30/00
CPC classification number: B01J37/031 , B01J23/755 , B01J37/08 , B01J37/18
Abstract: PURPOSE: Provided are a metal catalyst used for the fabrication of a carbon nano tube or a carbon nano fiber, and a method for fabricating the metal catalyst which is made of nickel, cobalt, iron or copper, or a mixture thereof. CONSTITUTION: The metal catalyst fabrication method comprises (a) adjusting pH of a metal sulfate aqueous solution containing at least one metal selected from a group consisting of nickel, cobalt, iron, and copper using ammonia solution, thereby settling metal hydroxides, and drying the settled metal hydroxides, (b) calcining the metal hydroxides to form metal oxides at a temperature in a range of 800-1000°C, and (c) reducing the metal oxides at hydrogen ambience.
Abstract translation: 目的：提供用于制造碳纳米管或碳纳米纤维的金属催化剂，以及由镍，钴，铁或铜制成的金属催化剂的制造方法或其混合物。 构成：金属催化剂的制造方法包括：（a）使用氨溶液调节含有选自镍，钴，铁和铜的至少一种金属的金属硫酸盐水溶液的pH值，由此沉淀金属氢氧化物，并干燥 沉淀的金属氢氧化物，（b）在800-1000℃的温度下煅烧金属氢氧化物以形成金属氧化物，和（c）在氢气氛下还原金属氧化物。
-
公开(公告)号：KR100356370B1
公开(公告)日：2002-10-19
申请号：KR1019990059882
申请日：1999-12-21
Applicant: 재단법인 포항산업과학연구원 , 제일연마공업주식회사
IPC: B24D3/00
Abstract: 본발명은연삭지석성형체에관한것으로서, 지석골재, 액상소결조제, 임시결합재, 결합강화제(wetting agent)등과같은연삭지석원료를혼합하는공정에서 Li, Na, K, Rb 등과같은알칼리금속또는 Be, Mg, Ca, Sr 등과같은알칼리토금속의수산화물을단독또는혼합하여첨가하는연삭지석성형체제조공정에서임시결합재로사용되는전분(dextrin)의중축합을촉진시킴과동시에중축합시의발열반응에기인한열을이용하여임시결합재의결합력을향상시켜, 성형체의초기강도를향상시키고, 성형체의운반자동화나성형체불량율을감소시킬수 있는연삭지석성형체에관한것이다.
-
-
-
-
-
-
-
-
-