Abstract:
PURPOSE: A magnetic ceramic composite for a microwave element, a magnetic ceramic for a microwave element using the same and a manufacturing method thereof are provided to manufacture a ceramic in an economic manner by reducing a sintering temperature to 1250 °C, or below and actually apply to a microwave substitute component by reducing a temperature coefficient of a saturated magnetization. CONSTITUTION: A compound of yttrium and iron oxide is a principle component. An accessory component is selected from the group consisting of zinc oxide, a compound of zinc oxide and boron oxide, and a compound of oxidized copper and boron oxide. A ceramic composite is manufactured by using the principle component and the accessory component. Yrritum and iron oxide are mixed and calcined. One among zinc oxide, a compound of zinc oxide and boron oxide, and a compound of oxidized copper and boron oxide is added to the mixture as an accessory component. A magnetic ceramic is manufactured by shape forming and sintering the mixture which is added with the accessory component.
Abstract:
PURPOSE: A device and method is provided to be applied to variety of optical devices like WDM and laser by using an eribum doped planar amplifier to reduce transfer loss and contact loss with optical fibers. CONSTITUTION: A device comprises an erbium doped core layer(ED), an erbium-undoped core layer(UD), an inputting element(1) a WDM coupler(2), a wave guide(3), a wave length separator(4), an anti-reflective angled wave guide(5), a lower clad layer(10), and an upper clad layer(12). A method comprises a step of forming the ER-undoped core layer on the lower clad layer; a step of forming defining the optical amplifier area by selectively etching the ER-undoped core layer; and a step of forming the ER-doped core layer at the optical amplifier area. The method further comprises a step of forming the wave guide at the optical amplifier area between the input part and the output part and a step of forming the upper clad layer at the whole structure.
Abstract:
본 발명은 민생용 및 산업용 전자기기에 사용되는 마이크로파 대역 부품용 소재에 관한 것으로, 포화자화의 제어가 용이하고 낮은 페리자성공명반치폭과 양호한 큐리온도를 지닌 마이크로파 소자용 자성체 세라믹 조성물, 이를 이용한 마이크로파 소자용 자성체 세라믹 및 그의 제조방법에 관한 것이다. 본 발명의 마이크로파 소자용 자성체 세라믹 조성물은, 산화이트륨, 산화철, 산화주석, 산화알루미늄 및 칼슘 공급원을 주성분으로 하고, 하기 조성식으로 표시되며, 본 발명에 따른 마이크로파 소자용 자성체 세라믹은, 하기 조성식에 따라, 산화이트륨, 산화철, 산화주석, 산화알루미늄 및 탄산칼슘(또는 산화칼슘)을 혼합한 후, 성형 및 소결하여 제조된 것으로, 상온에서 100~1,800 G의 포화자화와 3 G/℃ 이내의 포화자화 온도계수 및 60 Oe 이하의 페리자성공명반치폭을 지닌 것을 특징으로 한다: Y 3-x Ca x Sn x Fe 5-y Al y O 12 이때, 0.1≤x≤1 이고, 0.2≤y≤1.5이다.
Abstract:
a dielectric block (1) which has an internal conductor groove (8) in the center of the bottom and whose five faces except the upper face are plated with conductor; an electrode (7) which is attached in the center of the opened face of the dielectric block (1); a spare electrode (9) which is attached in both side of the electrode (7) to form an input/output capacitor.
Abstract:
The device grinds the outer surfaces of cylinders(1) having small holes on their centers at once. The device comprises a grinding disk(7) mounted on the top of shaft(8), a grinding paper(9) attatched to the grinding disk(7), and a plurality of jigs, which includes a cylindrical workpiece fixing frame(4), a plurality of wires(5) arranged in the fixing frame(4), a fixing metal(65) to stretching the wires(5), and a cover plate(10) to press the workpieces.
Abstract:
본 발명은 유극형 유전체 공진기 및 그의 결합구조에 관한 것으로, 상단면을 제외한 다섯면이 도체로 도금되며, 하단면에 내부도체용 홈(8)이 형성된 유전체 블럭(1); 및 상기 유전체블럭(1)의 상단면에 부착된 전극(7) 및 보조전극(9)을 구비하며, 대역통과 필터를 구성하기 위하여 상기의 구성에 제2 유전체필터(1')를 결합되는 결합구조를 갖도록 하므로서 단위공진기 자체가 노치용 직렬커패시턴스를 갖기 때문에 외부에 별도의 커패시터를 사용하지 않고도 유극형 필터를 제작할 수 있고, 주파수특성 향상과 소형화 및 가격이 절감되는 효과가 있다.
Abstract:
본 발명은 14∼20mol%의 산화바륨(BaO) 또는 탄산바륨(BaCO 3 ), 9.4∼20mol%의 산화사마륨(Sm 2 O 3 ), 0.5∼6.3mol%의 산화란탄늄(La 2 O 3 ), 60∼72mol%의 이산화티탄(TiO 2 )을 주성분으로하고 여기에 부성분을 0.05∼2wt%를 첨가하여 형성되는 것을 특징으로 하는 마이크로웨이브용 유전체 세라믹 조성물에 관한것으로, 이때 상기 부성분을 산화동과 티탄산을 합성한 티탄산동(CuTiO 3 ), 산화동과 산화붕소를 합성한 CuB 2 O 4 또는 Cu 2 B 2 O 5 중 어느 하나로 이루어진다. 이렇게하여 형성된 조성물은 상온에서 70 이상의 유전률과 ±5ppm/℃ 이내의 공진주파수 온도계수 및 높은 품질계수를 갖는 유전체를 얻을 수 있고, 이들 유전체는 온도특성이 우수하기 때문에 마이크로웨이브 유전체에 응용가능하며, 공진주파수 온도계수가 ±300ppm/℃ 이내를 갖는 유전체는 EMI 필터용 유전체 및 온도보상용 커패시터로 널리 이용할 수 있다. 또한, 소결온도를 낮출 수 있기 때문에 제조원가를 절감할 수 있는 효과가 있다.