公开(公告)号：KR1020090027332A
公开(公告)日：2009-03-17
申请号：KR1020070092474
申请日：2007-09-12
Applicant: 한국전기연구원
CPC classification number: H01M4/366 , C01B25/45 , H01M4/5825 , H01M4/583 , H01M10/052 , H01M2004/028 , Y02E60/122
Abstract: A method for manufacturing an active material is provided to simplify a synthesis process of an active material and to save the processing costs of the active material and lithium secondary battery by using an active material as an inexpensive starting material. A method for manufacturing an active material of the chemical formula 1: Li_xA_(1-x)Fe_yB_(1-y)(PO_4)_zC_(1-z), comprises a step for preparing a mixture containing FePO4, lithium salt and a reducing agent; a step for preparing the slurry by pulverizing the mixture with a ball mill; a step for heat-treating the slurry under inert gas. In the chemical formula 1,
Abstract translation: 提供一种制造活性材料的方法，以简化活性材料的合成过程，并通过使用活性材料作为廉价的起始材料来节省活性材料和锂二次电池的加工成本。 制备化学式1：Li_xA_（1-x）Fe_yB_（1-y）（PO_4）_zC_（1-z）的活性材料的方法包括制备含有FePO 4，锂盐和还原剂的混合物的步骤 剂; 通过用球磨机粉碎混合物来制备浆料的步骤; 在惰性气体下热处理浆料的步骤。 在化学式1中，
-
公开(公告)号：KR1020090006934A
公开(公告)日：2009-01-16
申请号：KR1020070070404
申请日：2007-07-13
Applicant: 한국전기연구원
Abstract: A method for solidifying carbon dioxide is provided to save processing cost and processing time by reacting treated material electrolyzed using salt water or sea water and carbon dioxide generated in generating station and forming carbonate. A method for solidifying carbon dioxide includes steps of: electrolyzing salt water or sea water and forming treated material including hydrogen(H2), chlorine(Cl2) and basic solution; collecting the hydrogen and the chlorine in the treated material generated in the first step; reacting a basic solution the treated material generated in the first step with the collected carbon dioxide and forming carbonate; and collecting the carbonate generated in the third step.
Abstract translation: 提供一种固化二氧化碳的方法，通过使用盐水或海水电解的处理材料和在发电站中产生的二氧化碳和形成碳酸盐反应，来节省加工成本和加工时间。 一种固化二氧化碳的方法包括以下步骤：电解盐水或海水，并形成处理过的材料，包括氢（H 2），氯（Cl 2）和碱性溶液; 收集在第一步产生的处理过的材料中的氢气和氯气; 将碱性溶液与第一步产生的处理物料与收集的二氧化碳反应并形成碳酸盐; 并收集第三步产生的碳酸盐。
-
公开(公告)号：KR100839443B1
公开(公告)日：2008-06-19
申请号：KR1020070021243
申请日：2007-03-05
Applicant: 한국전기연구원
CPC classification number: H01M12/065 , H01M2/0275 , H01M2/162 , H01M2/1653 , H01M4/42 , H01M4/623 , H01M4/625 , H01M4/661 , H01M4/74 , H01M4/9016 , H01M2300/0085
Abstract: A method for preparing a flexible zinc air battery, and a flexible zinc air battery prepared by the method are provided to reduce the weight of a battery, thereby improving energy density remarkably and to allow it to be bent smoothly. A method for preparing a flexible zinc air battery comprises the steps of compressing a film(6) comprising an aluminum thin film and a polymer with a jig to form a lower case so as to allow an electrolyte gel to be put; placing a copper thin film on bottom and putting an electrolyte gel comprising a zinc powder(5), a gelled polymer and a KOH aqueous solution; covering a polypropylene polymer film(4) as a separator on the electrolyte gel and layering a positive electrode(1) and nonwoven(3) in turn; punching a hole(9) to an upper film made of the polymer identical to the polymer film used in the lower case so as to allow air to penetrate and adhering its upper part with a sealing tape(7) to block the penetration air, thereby preparing an upper case; and heat compressing the upper case and the lower case at 150 deg.C or more to adhere them.
Abstract translation: 提供一种制备柔性锌空气电池的方法和通过该方法制备的柔性锌空气电池，以减轻电池的重量，从而显着提高能量密度并使其平滑地弯曲。 制备柔性锌空气电池的方法包括以下步骤：用夹具压缩包含铝薄膜和聚合物的薄膜（6）以形成下壳体，以便放置电解质凝胶; 将铜薄膜放置在底部并放置包含锌粉（5），胶凝聚合物和KOH水溶液的电解质凝胶; 将聚丙烯聚合物膜（4）作为隔膜覆盖在电解质凝胶上，依次层叠正极（1）和无纺布（3）; 将孔（9）冲压到由与下壳体中使用的聚合物膜相同的由聚合物制成的上膜，以便空气用密封带（7）渗透并粘附其上部以阻挡渗透空气，由此 准备大写; 并将上壳体和下壳体在150摄氏度或更高温度下进行热压粘合。
-
公开(公告)号：KR100788257B1
公开(公告)日：2007-12-27
申请号：KR1020070019373
申请日：2007-02-27
Applicant: 한국전기연구원
CPC classification number: H01M4/366 , H01M4/5805 , H01M4/622 , H01M4/625 , H01M4/667 , H01M10/0525 , Y02E60/122
Abstract: A high voltage lithium secondary battery is provided to improve the discharge capacity and cycle characteristics even in case of the high voltage charge process. A high voltage lithium secondary battery comprises a positive electrode which comprises a positive electrode active material, a conductive material, and a binder in a ratio of 90-98 : 1-5 : 1-5 by weight; a negative electrode which comprises a Sn_a Cu_b-graphite composite (wherein a:b is 3:8 to 8:3); and an ion conductor. The positive electrode active material is a LiCoO2 active material formed by coating it with Co3(PO4)2 so as to form a LiCoPO4 thin film on the surface; the conductive material is carbon black (super P black); and the binder is polyvinylidene fluoride.
Abstract translation: 提供高压锂二次电池，以提高放电容量和循环特性，即使在高电压充电过程的情况下也是如此。 高压锂二次电池包括正极，其包含正极活性物质，导电材料和粘合剂，其比例为90-98:1〜5:1〜1-5重量比; 负极，其包含Sn_a Cu_b-石墨复合材料（其中a：b为3:8至8:3）; 和离子导体。 正极活性物质是通过用Co 3（PO 4）2涂覆而形成的LiCoO 2活性物质，以在表面上形成LiCoPO 4薄膜; 导电材料为炭黑（超P黑）; 粘合剂为聚偏二氟乙烯。
-
公开(公告)号：KR1020070094721A
公开(公告)日：2007-09-21
申请号：KR1020070091734
申请日：2007-09-10
Applicant: 한국전기연구원
Abstract: A method for preparing an electrode active material of an energy storage device, an electrode active material prepared by the method, an electrode using the electrode active material, and an energy storage device containing the electrode active material are provided to increase the interlayer distance of carbon remarkably, thereby improving the capacitance per volume and reducing the expansion of an electrode the application of voltage. A method for preparing an electrode active material comprises the steps of a heat treating a carbon material for pretreatment; oxidizing the pretreated carbon material with oxygen; optionally washing the oxidized carbon material; and optionally heat treating the oxidized carbon material for reduction. Preferably the pretreatment is carried out under the inert gas atmosphere at a temperature of 300-2,000 deg.C fur 2-24 hours; and the oxidation is carried out by oxidizing a carbon material in s mixture solution containing an oxidizing agent. Preferably the carbon material is a graphitizable carbonaceous material or contains a graphitizable carbonaceous material.
Abstract translation: 提供一种制备储能装置的电极活性材料的方法，通过该方法制备的电极活性材料，使用该电极活性材料的电极和含有该电极活性材料的储能装置，以增加碳的层间距离 显着地提高了每体积的电容量，并降低了电极的施加电压。 制备电极活性材料的方法包括以下步骤：用于预处理的碳材料的热处理; 用氧氧化预处理的碳材料; 任选地洗涤氧化碳材料; 并且可选地将氧化的碳材料热处理以进行还原。 优选地，预处理在惰性气体气氛下在300-2000℃皮皮2-24小时进行; 通过氧化含有氧化剂的混合溶液中的碳材料进行氧化。 优选地，碳材料是可石墨化的碳质材料或含有可石墨化的碳质材料。
-
Patent Agency Ranking
公开(公告)号：KR1020070087481A
公开(公告)日：2007-08-28
申请号：KR1020060108588
申请日：2006-11-03
Applicant: 한국전기연구원
Abstract: Provided are a method for preparing an electrode active material to improve the capacity per volume and to reduce the expansion of an electrode due to the application of voltage, an electrode active material prepared by the method, an electrode for an energy storage electrode containing the active material, and an energy storage electrode containing the electrode. A method comprises the steps of heat-treating a carbon product for pretreatment; oxidizing the pretreated carbon product with an oxidizing agent; optionally washing the oxidized carbon product; and optionally heat-treating the oxidized carbon product for reduction. Preferably the pretreatment is carried out at a temperature of 300-2,000 deg.C for 2-24 hours under the inert gas atmosphere; and the carbon product is oxidized by dipping it in a mixture solution containing an oxidizing agent.
Abstract translation: 提供了一种制备电极活性材料的方法，以提高每单位体积的容量和减少由于施加电压引起的电极的膨胀，通过该方法制备的电极活性材料，包含活性物质的储能电极用电极 材料和含有电极的储能电极。 一种方法包括对预处理的碳产品进行热处理的步骤; 用氧化剂氧化预处理的碳产物; 任选地洗涤氧化碳产物; 并任选地将氧化的碳产物热处理以进行还原。 优选地，预处理在惰性气体气氛下在300-2000℃的温度下进行2-24小时; 并且通过将碳产物浸渍在含有氧化剂的混合溶液中而将其碳氧化。
-
公开(公告)号：KR100583672B1
公开(公告)日：2006-05-26
申请号：KR1020040041258
申请日：2004-06-07
Applicant: 한국전기연구원
IPC: H01M4/04
CPC classification number: H01M10/052 , H01M4/0404 , H01M4/043 , H01M4/131 , H01M4/1391 , H01M4/622
Abstract: 본 발명에 따른 리튬이차전지용 고출력 극판의 제조방법은, 에틸렌 카보네이트(ethylene carbonate:EC) 결정을 적당한 용매에 녹여 EC 용액을 만드는 단계; 결합제를 적당한 용매에 녹여 결합제 용액을 만든 후, 이 용액에 원하는 조성의 전극 활물질과 도전재를 첨가하여 충분히 섞어주는 단계; 상기 결합제 용액에 상기 미리 만들어 둔 EC 용액을 소정량 첨가하고 충분히 교반하여 전극에 도포할 전극합제로서의 슬러리(slurry)를 만드는 단계; 슬러리를 집전체에 도포하고 소정 온도에서 충분히 건조시키는 단계; 및 건조 과정 완료 후, 건조된 극판 구조체를 소정의 압력으로 압착하여 최종 극판을 제조하는 단계를 포함하여 구성된다.
이와 같은 본 발명에 의하면, EC를 이용하여 극판 내에 미세 공동을 형성하여 고출력 극판을 만들어 줌으로써 이를 채용한 전지의 수명 특성과 방전 특성을 크게 개선할 수 있다. 또한, 환경호르몬인 DBP 등을 사용하지 않고, 메탄올, 에테르 등을 사용한 별도의 추출 공정 없이 그대로 전지 제조가 가능하므로, 공정에 소요되는 비용과 시간을 절감할 수 있고, 작업상의 안전성을 높일 수 있으며, 환경 오염 방지의 효과도 거둘 수 있다.
리튬2차전지, 극판Abstract translation: 制造锂二次电池用高功率电极的方法考虑（a）通过将EC晶体溶解在合适的溶剂中制备EC（碳酸亚乙酯）溶液; （b）将粘合剂溶解在合适的溶剂中以制备粘合剂溶液，然后将粘合剂溶液，活性电极材料和所需组成的导电材料加入并充分混合; （c）将步骤（a）中制备的预定量的EC溶液加入到步骤（b）中获得的粘合剂溶液中; （d）充分搅拌EC溶液和粘合剂溶液的混合物以制备作为电极粘合剂的浆料以涂覆在电极上; （e）将浆料涂布在收集器上; （f）在预定温度下充分干燥涂覆的浆料; 和（g）在涂覆的浆料干燥之后，通过在预定压力下压缩干燥的电极结构来制造最终电极。
-
公开(公告)号：KR100559770B1
公开(公告)日：2006-03-10
申请号：KR1020030078966
申请日：2003-11-10
Applicant: 한국전기연구원
IPC: H01M4/58
Abstract: 본 발명에 따른 리튬 2차전지용 양극 활물질의 제조방법은, 소정의 용매에 녹을 수 있는 니켈(Ni), 코발트(Co), 철(Fe)의 금속 화합물을 용해하여 원하는 금속이온이 있는 용액을 만드는 단계; 상기 용액에 원하는 당량비의 리튬(Li) 이온이 함유된 용액과 전체 금속이온의 소정 당량비의 수산기(OH(-))를 첨가하여 금속이온을 수산화물로 침전시키는 단계; 침전물이 함유된 용액을 여과함 없이 그대로 소정 온도에서 증발, 건조하여 원하는 당량비의 금속 수산화물들의 혼합체를 얻는 단계;상기 수산화물 혼합체를 가분쇄하여 분말상태로 만들고, 여기에 순수한 에탄올을 극소량 첨가한 후 잘 반죽하여 진흙과 같은 상태로 전구체를 만드는 단계; 및 상기 금속 수산화물 진흙 전구체를 소정 온도에서 하소 공정을 거친 후 가분쇄하고, 이 분말을 테블릿 성형 없이 그대로 소정 온도에서 최종 열처리하여 균일상을 가지는 최종 금속 산화물 분말을 제조하는 단계를 포함하여 구성된다.
이와 같은 본 발명에 의하면, 종래 재료에 비해 산화물 구조가 안정하고 비수계 유기 전해액과의 반응성이 매우 낮아, 전지의 발열량을 대폭 낮추고 전지내부에서의 가연성 기체 발생을 억제하여 비정상적인 사용환경 하에서도 전지의 안전성을 크게 향상시킬 수 있다. 따라서, 열악한 조건하에서도 안전성이 크게 향상된 리튬 2차전지를 제조할 수 있는 장점이 있다.-
公开(公告)号：KR100524558B1
公开(公告)日：2005-10-28
申请号：KR1020040013617
申请日：2004-02-27
Applicant: 한국전기연구원
IPC: H01M4/58
Abstract: 본 발명에 따른 리튬 2차전지용 양극 활물질의 제조방법은, LiNi
x Mn
y Si
1-xy O
2 또는 LiNi
x Mn
y Co
z Si
1-xyz O
2 의 조성을 갖는 산화물을 제조하기 위하여 리튬(Li), 니켈(Ni), 망간(Mn), 코발트(Co)를 함유한 금속화합물을 용매에 녹여 원하는 금속 이온이 있는 용액을 만드는 단계; 상기 용액에 원하는 당량비의 규소(Si) 이온이 함유된 용액을 침적하는 단계; 상기 원하는 금속 이온과 규소 이온이 함유된 용액을 그대로 소정 온도에서 증발, 건조하여 원하는 당량비의 금속/비금속 화합물의 혼합체를 얻는 단계; 상기 금속/비금속 혼합체를 가분쇄하여 분말상태로 만들고, 여기에 순수한 에탄올을 극소량 첨가한 후 잘 반죽하여 진흙과 같은 상태로 전구체를 만드는 단계; 및 상기 에탄올 첨가에 의해 생성된 금속 수산화물 진흙 전구체를 소정 온도에서 하소 공정을 거친 후 가분쇄하고, 이 분말을 테블릿 성형 없이 그대로 소정 온도에서 최종 열처리하여 균일상을 가지는 최종 금속 산화물 분말을 제조하는 단계를 포함한다.
이와 같은 본 발명에 의하면, 제조된 양극활물질이 매우 큰 격자상수를 가져전지의 율특성을 개선할 수 있고, 산화물의 격자크기의 변화율이 적고 전지의 내부저항 증가율이 크지 않기 때문에 전지의 수명 특성을 크게 개선할 수 있다.-
公开(公告)号：KR100461876B1
公开(公告)日：2004-12-14
申请号：KR1020020030929
申请日：2002-06-01
Applicant: 한국전기연구원 , 에너테크인터내셔널 주식회사
IPC: H01M10/05
CPC classification number: H01M10/0565 , H01M10/0525 , H01M10/058
Abstract: 본 발명은 고전압 및 고에너지를 가지며 사이클 특성이 우수하면서도 겔의 물성조절이 용이한 겔폴리머전해질을 사용한 리튬이온전지를 제조하는 방법을 제공하기 위한 것이다. 본 발명의 리튬이온전지 제조방법은, 리튬이온을 삽입·탈삽입할 수 있는 활물질을 함유하는 양극층 및 음극층이 각각 양극집전체 및 음극집전체 위에 놓여 있고 상기 양극층과 음극층 사이에 분리막이 개재되어 있는 전극 적층구조에, 전해액과 폴리우레탄아크릴레이트계 매크로머를 포함하는 전구체를 주입한 후에 열중합시켜 겔상 전해질로 만드는 것을 특징으로 한다.
Abstract translation: 目的：提供一种制备锂离子电池的方法，以获得使用具有高电压，高能量，优异的循环特性和物理性质的凝胶电解质的锂离子电池，以便容易地控制。 组成：该方法包括以下步骤：将包含电解质溶液的前体插入到包含正极层（2）和负极层（4）的电极层压结构中，所述正极层（2）和负极层（4）包含能够嵌入或取出锂离子的活性材料和 分别放置在正极集电体（1）和负极集电体（5）上，隔膜（3）位于正极层和负极层之间; 并将前体热聚合以制备凝胶相电解质。 优选地，将电极层压结构插入铝层压膜（6）中，插入包含反应性单体和大分子单体之间的任何一种的前体和电解质溶液，并使前体热聚合。
-
-
-
-
-
-
-
-
-