公开(公告)号：KR100974542B1
公开(公告)日：2010-08-11
申请号：KR1020080112703
申请日：2008-11-13
Abstract: 본 발명은 신가스(syngas)를 이용하여 액체탄화수소를 제조하기 위해 철계 촉매(조성비율 Fe/Cu/Al/K = 100/6/16/4 중량부) 및 C
5 -C
7 의 노말탄화수소 초임계 유체를 사용한 피셔-트롭쉬(Fischer-Tropsch, FT) 합성 방법에 관한 것이다. 본 발명에 따른 피셔-트롭쉬 합성 방법은 초임계 유체를 사용하여 기존의 탄화수소 제조방법에서 사용하는 기상반응에 비해 유사한 일산화탄소의 전환율을 나타내나, 이산화탄소 및 메탄의 발생량을 대폭 감소시켜 C
5 이상의 탄화수소의 선택도 및 올레핀의 선택도를 증대시킬 수 있다.
피셔-트롭쉬 합성반응, 액체탄화수소, C5-C7의 노말탄화수소 초임계 유체, 철계 촉매-
92.发明公开
公开(公告)号：KR1020100001287A
公开(公告)日：2010-01-06
申请号：KR1020080061147
申请日：2008-06-26
Abstract: PURPOSE: A water dispersible acrylic polymer emulsion composition is provided to improve a crosslinking property compared with an existing method and to prepare coating fertilizer with excellent dissolution rate control that release the fertilizer slowly in an aqueous phase. CONSTITUTION: A water dispersible acrylic polymer emulsion composition for coating granular urea fertilizer is obtained by adding an acrylic functional crosslinkable monomer, a silane cross-linking agent or their mixture to a water dispersible acrylic polymer emulsion composition containing an initiator and emulsifier during emulsion polymerization in an acrylic monomer aqueous solution.
Abstract translation: 目的：提供水分散性丙烯酸聚合物乳液组合物以改善与现有方法相比的交联性能，并制备具有优异溶出速率控制的涂层肥料，其在水相中缓慢释放肥料。 构成：通过在丙烯酸官能交联单体，硅烷交联剂或其混合物中将乳液聚合中含有引发剂和乳化剂的水分散性丙烯酸类聚合物乳液组合物中加入丙烯酸官能交联单体，得到用于涂布颗粒状尿素肥料的水分散性丙烯酸类聚合物乳液组合物 丙烯酸单体水溶液。
-
公开(公告)号：KR100693362B1
公开(公告)日：2007-03-09
申请号：KR1020050112497
申请日：2005-11-23
Applicant: 한국화학연구원
Abstract: A crystalline molecular sieve with a mesoporous structure which has a large pore size, a thick thickness of a pore wall and improved hydrothermal stability, a preparation method of the crystalline molecular sieve, a catalyst for dearomatization of residue oil after naphtha cracking using the crystalline molecular sieve, and a method for preparing the catalyst using the crystalline molecular sieve are provided. A method for preparing a crystalline molecular sieve with a mesoporous structure comprises the steps of: (a) dissolving 1 to 30 weight parts of silica or aluminum salt, or a mixture of the silica or aluminum salt and a metal alkoxide selected from titanium alkoxide, aluminum alkoxide and silicon alkoxide into 100 weight parts of a hydrogen fluoride solution with a concentration of 10 to 60%, wherein the mixture has an Si/metal molar ratio of 5 to 100; (b) dissolving 2 to 30 weight parts of a mixture of a nonionic surfactant and trialkylbenzene into 100 weight parts of distilled water; (c) uniformly mixing the solution prepared in the step(a) with the solution prepared in the step(b) at a weight ratio of 1:0.5 to 2.0, adding 20 to 30 weight parts of ammonia water with a concentration of 20 to 30 wt.% relative to 100 weight parts of the hydrogen fluoride solution to the mixed solution, aging the resulting solution at 25 to 90 deg.C for 16 to 24 hours, and filtering and drying the aged solution to prepare powder; and (d) mixing the powder with 200 to 400 weight parts of an acidic ethanol solution in which an acid selected from hydrochloric acid, sulfuric acid and nitric acid is dissolved relative to 100 weight parts of the hydrogen fluoride solution to clean the powder prepared in the step(c), drying the cleaned powder, and calcining the dried powder at 300 to 600 deg.C.
Abstract translation: 一种具有孔径大，孔壁厚度厚，水热稳定性好的介孔结构的结晶分子筛，结晶分子筛的制备方法，石脑油裂解后使用结晶分子的渣油脱芳化催化剂 筛，以及使用结晶分子筛制备催化剂的方法。 制备具有介孔结构的结晶分子筛的方法包括以下步骤：（a）将1-30重量份的二氧化硅或铝盐，或二氧化硅或铝盐与选自钛醇盐， 铝醇盐和硅醇盐加入100重量份浓度为10-60％的氟化氢溶液中，其中混合物的Si /金属摩尔比为5-100; （b）将2至30重量份的非离子表面活性剂和三烷基苯的混合物溶解于100重量份的蒸馏水中; （c）将步骤（a）中制备的溶液与步骤（b）中制备的溶液以1:0.5至2.0的重量比均匀混合，加入20至30重量份浓度为20至30的氨水 相对于100重量份的氟化氢溶液30重量％添加到混合溶液中，在25〜90℃下使所得到的溶液老化16〜24小时，过滤并干燥该老化后的溶液，从而制备粉末。 （d）将粉末与相对于100重量份的氟化氢溶液溶解有200-400重量份的酸性乙醇溶液（其中溶解有选自盐酸，硫酸和硝酸中的酸）以清洁在 步骤（c），干燥清洁后的粉末，并在300-600℃煅烧干燥的粉末。
-
公开(公告)号：KR100639788B1
公开(公告)日：2006-10-30
申请号：KR1020050029160
申请日：2005-04-07
Applicant: 한국화학연구원
Inventor： 정순용
Abstract: 본 발명은 층상실리케이트를 주형으로 이용하여 제조된 다공성 흑연과 이의 제조방법에 관한 것으로서, 더욱 상세하게는 층상실리케이트의 층간에 전이금속 화합물과 유기 탄소화물을 삽입한 후, 열 분해하여 층상 실리케이트의 층 사이에 다공성 결정형 흑연층이 교대로 적층된 구조를 이루고 있는 나노복합체를 얻은 다음, 실리케이트 골격과 흑연층 내부에 분산된 전이금속 이온을 용출 제거하는 방법으로, 균일한 크기의 옆상(plate)입자로 구성되고, 개개의 입자는 결정형 흑연층이 겹겹이 규칙적으로 배열된 적층 구조를 이루고, 각 층간 간격은 충분히 확보되어 있으며, 흑연층 사이의 공간이 다공성을 나타내는 구조적 특징을 가진 다공성 흑연과 이의 제조방법에 관한 것이다.
층상실리케이트, 전이금속 화합물, 유기 탄소화물, 다공성 흑연-
公开(公告)号：KR100408006B1
公开(公告)日：2003-12-03
申请号：KR1020010033161
申请日：2001-06-13
Applicant: 에스케이 인천정유 주식회사 , 한국화학연구원
IPC: C01B39/02
Abstract: PURPOSE: An improved method for preparing mesoporous crystalline molecular sieve having large pore size and superior hydrothermal stability is provided. CONSTITUTION: The method for preparing mesoporous crystalline molecular sieve comprises the steps of a) preparing a first solution by dissolving 2 to 20 weight parts of silica alone or a mixture of silica and a metal salt or metal alkoxide into 100 weight parts of a hydrogen fluoride solution having concentration of 5 to 50%, wherein a mole ratio of Si/metal is 10 or more; b) preparing a second solution by dissolving 2 to 12 weight parts of cationic surfactant into 100 weight parts of distilled water; c) uniformly mixing the solutions by adding the first solution to the second solution in a weight ratio of 1 to 2:1 (second solution/first solution), and preparing powder by filtering and drying the aged solution after aging the resulting solution at a temperature of 25 to 80 deg.C for 10 to 18 hours by adding 20 to 30 weight parts of concentrated aqueous ammonia (based on 100 weight parts of the hydrogen fluoride solution) to the mixed solution; and d) adding the powder to 200 to 300 weight parts (based on 100 weight parts of the hydrogen fluoride solution) of an ethanol acidic solution, and calcining the resulting material at a temperature of 300 to 600 deg.C for 2 to 4 hours.
Abstract translation: 目的：提供一种制备具有大孔径和优异的水热稳定性的中孔结晶分子筛的改进方法。 构成：制备介孔结晶分子筛的方法包括以下步骤：a）通过将2至20重量份的单独的二氧化硅或二氧化硅与金属盐或金属醇盐的混合物溶解于100重量份的氟化氢 浓度为5至50％的溶液，其中Si /金属的摩尔比为10或更大; b）通过将2至12重量份的阳离子表面活性剂溶解于100重量份的蒸馏水中来制备第二溶液; c）通过将第一溶液以1：2：1的重量比（第二溶液/第一溶液）加入到第二溶液中来均匀地混合溶液，并且通过过滤和干燥老化的溶液来制备粉末， 通过将20至30重量份的浓氨水（基于100重量份的氟化氢溶液）加入到混合溶液中，在25至80℃的温度下进行10至18小时; 和d）将粉末加入到乙醇酸性溶液200-300重量份（基于100重量份氟化氢溶液）中，并将所得材料在300-600℃的温度下煅烧2-4小时 。
-
Patent Agency Ranking
公开(公告)号：KR100280376B1
公开(公告)日：2001-02-01
申请号：KR1019980032993
申请日：1998-08-14
Applicant: 한국화학연구원
IPC: C01B33/32
Abstract: 본 발명은 결정성 층상 이규산나트륨의 개량된 제조방법에 관한 것으로서, 더욱 상세하게는 일정 조성비의 무수 이규산나트륨 컬릿(cullet)분말을 출발물질로 하여 여기에 바인더로서 물 또는 규산나트륨 수용액을 가하여 조립 입상물을 조제하고 이를 결정화시키는 과정에 최소한의 최종제품을 재순환(recycle)시킴으로써, 연속공정중에 고온의 결정화 조건에서 발생하는 국부적인 소결현상으로 인해 반응물이 결정화 장치 내부에 부착되는 현상을 제거할 수 있을 뿐만 아니라, 최소량의 최종제품만을 재순환함으로써 대량생산시 기존방법에 비해 단위 생산성을 대폭 증가시키는 효과가 있는 결정성 층상 이규산나트륨의 개량된 제조방법에 관한 것이다.
-
公开(公告)号：KR100252463B1
公开(公告)日：2000-04-15
申请号：KR1019970071292
申请日：1997-12-20
Applicant: 한국화학연구원
IPC: B01J20/26
Abstract: PURPOSE: Provided is a manufacturing method of a granular complex agent for wastewater treatment exhibiting molecular sieving effect for the application to advanced wastewater treatment. CONSTITUTION: The manufacturing method of the granular complex agent comprises the steps of blending zeolite 10-70wt.% with activated carbon 10-90wt.%; injecting an alkali metal silicate solution thereto, followed by mixing for granulation; treating the obtained granule with an alkali earth metal salt solution, followed by treating with phosphate solution of 1-10wt.%; washing, filtrating, and drying; calcining the granule under reductive gas conditions ranging from 500 to 800deg.C for 0.5-10hrs.
Abstract translation: 目的：提供用于废水处理的颗粒状复合剂的制造方法，其具有用于高级废水处理的分子筛分效应。 构成：颗粒状复合剂的制造方法包括将10-70wt％的沸石与10-90wt。％活性炭共混的步骤; 向其中注入碱金属硅酸盐溶液，然后混合制粒; 用碱土金属盐溶液处理得到的颗粒，然后用1-10重量％的磷酸盐溶液处理; 洗涤，过滤和干燥; 在500至800℃的还原气体条件下煅烧颗粒0.5-10小时。
-
公开(公告)号：KR1019990014990A
公开(公告)日：1999-03-05
申请号：KR1019970036851
申请日：1997-08-01
Applicant: 한국화학연구원
IPC: C01B33/023
Abstract: 본 발명은 층상 나트륨마가다이트의 제조방법에 관한 것으로서, 더욱 상세하게는 실리카원과 알칼리원을 각각 별도로 투입하는 대신에 규산나트륨 수용액을 원료물질로 사용하여 수용액상에서 수열합성시키는 간단한 방법에 의해 나트륨마가다이트로 제조하는 방법으로, 기존방법에 비하여 제품의 순도를 높이고 반응시간을 단축시켜 에너지 소모를 획기적으로 줄일 수 있고, 값싼 원료물질을 사용하고 수율을 극대화함으로써 원가절감 효과를 얻을 수 있는 결정성 층상실리케이트의 일종인 층상 나트륨마가다이트의 제조방법에 관한 것이다.
-
公开(公告)号：KR1019990009359A
公开(公告)日：1999-02-05
申请号：KR1019970031732
申请日：1997-07-09
Applicant: 한국화학연구원
Abstract: 본 발명은 탈취제용 입상 복합 분자체와 그 제조방법에 관한 것으로서, 더욱 상세하게는 각종 형태의 제올라이트와 활성탄의 혼합물에 알칼리 금속 실리케이트 수용액을 배합하여 입상화시킨 복합 분자체 조성물에 구리, 철, 아연 및 알루미늄 등의 활성금속을 담지시킴으로써 악취 원인 가스를 흡착 제거하는 흡착 특성이 우수하고, 획기적인 흡착량 증가로 인한 장기간 사용이 가능하며, 식품 사용에 있어서 신선도 유지 기능 등의 매우 유용한 특성을 가지고 있어서 냉장고, 음식물 쓰레기 처리기, 화학 공장 및 동물 사육장 등에서 발생하는 악취 제거 및 공기 정화에 유용한 탈취제용 입상 복합 분자체와 그 제조방법에 관한 것이다.
-
公开(公告)号：KR1019960007542A
公开(公告)日：1996-03-22
申请号：KR1019940020113
申请日：1994-08-14
Applicant: 한국화학연구원
IPC: C07C217/78
Abstract: 본 발명은 4-클로로-2,5-디알콕시 니트로벤젠을 아세토 니트릴 또는 그의 수용액을 용매로 하여 촉매의 황화처리 여부에 관계없이 백금계 담지 촉매하에 수소환원시켜 탈염소화 없이 4-클로로-2,5-디알콕시 아닐린을 제조하는 방법에 관한 것이며 또한 생성 혼합물을 산석(酸析) 또는 염석(鹽析)을 통해 정제함으로써 반응물의 순도에 관계없이 고순도의 4-클로로-2,5-디알콕시 아닐린을 얻는 정제 방법에 관한 것이다.
-
-
-
-
-
-
-
-
-