公开(公告)号：KR101134564B1
公开(公告)日：2012-04-19
申请号：KR1020100121581
申请日：2010-12-01
Applicant: 목포대학교산학협력단
Inventor： 이상진
CPC classification number: C09D1/02 , C08K3/04 , C08K3/22 , C08K3/32 , C08K3/34 , C08K3/36 , C08K2003/2241 , C09D5/00
Abstract: PURPOSE: A ceramic heat-resistant paint composition is provided to easily form a coating at room temperature, to remarkably reduce the generation of smell, and to have high adhesion and heat resistance at high temperatures, thereby preventing the damage of base material due to thermal transformation even at high temperatures. CONSTITUTION: A ceramic heat-resistant paint composition comprises: liquid type potassium silicate sol mixed of potassium oxide, silicon dioxide, phosphoric acid and water; ceramic powder which is added and mixed into the potassium silicate sol, mixed of vermiculite, titanium dioxide and zircon; and graphite which is added after mixing the potassium silicate sol and the ceramic powder. The potassium silicate sol and the ceramic powder have the mixing ratio of 60-80 wt% and 20-40 wt%.
Abstract translation: 目的：提供陶瓷耐热涂料组合物以在室温下容易地形成涂层，显着减少气味的产生，并且在高温下具有高的粘附性和耐热性，从而防止由于热而导致的基体材料的损坏 即使在高温下也能转变。 构成：陶瓷耐热涂料组合物包括：混合氧化钾，二氧化硅，磷酸和水的液态硅酸钾溶胶; 添加并混合到硅酸钾溶胶中的陶瓷粉末，混合蛭石，二氧化钛和锆石; 和混合硅酸钾溶胶和陶瓷粉末后加入的石墨。 硅酸钾溶胶和陶瓷粉末的混合比例为60-80重量％和20-40重量％。
-
公开(公告)号：KR101074152B1
公开(公告)日：2011-10-17
申请号：KR1020100087470
申请日：2010-09-07
Applicant: 목포대학교산학협력단
CPC classification number: C01F17/0043 , C01P2002/72 , C01P2004/03 , C01P2004/04
Abstract: 본 발명은 낮은 온도에서 합성되며, 고순도, 다공성의 물성을 갖는 yttria 분말의 합성 방법에 관한 것으로, 출발원료인 Yttrium nitrate(Y(NO
3 )
3 9H
2 O)를 준비하는 단계, 상기 출발원료를 증류수에 용해시키는 단계, 상기 증류수에 PVA(Polyvinyl alcohol) 용액을 첨가하여 Yttrium 전구체를 형성하는 단계, 상기 전구체를 열 교반 및 건조시켜 겔 타입(gel-type)의 전구체를 형성하는 단계 및 상기 PVA를 제거하고 나노결정구조를 갖도록 상기 전구체를 열처리하는 단계를 포함한다.-
公开(公告)号：KR1020110032943A
公开(公告)日：2011-03-30
申请号：KR1020090090714
申请日：2009-09-24
Applicant: 목포대학교산학협력단
IPC: A44C25/00 , A44C27/00 , A61K35/618 , B44C5/06
CPC classification number: A44C25/00 , A44C27/00 , A61K35/618 , B44C5/06
Abstract: PURPOSE: An accessory using cuttlefish bone and a manufacturing method thereof are provided to reinforce the intensity of the accessory through primer coating. CONSTITUTION: A manufacturing method of an accessory using the cuttlefish bone comprises: a step of removing smell by washing the cuttlefish bone using ethanol; a step of molding by cutting and processing the cuttlefish bone from which smell is removed; a step of coloring the molded cuttlefish bone with dye; and a step of reinforcing the colored cuttlefish bone through primer coating. The ethanol washing is performed using an ultrasonic cleaner for 3-5 hours.
Abstract translation: 目的：提供使用墨鱼的附件及其制造方法，以通过底漆涂布来增强附件的强度。 构成：使用乌贼骨的附件的制造方法包括：通过使用乙醇洗涤乌贼骨来除去气味的步骤; 通过切割和加工除去臭味的墨鱼骨成型的步骤; 用染料着色成型的乌贼骨的步骤; 以及通过底漆涂布来加强着色的乌贼骨的步骤。 乙醇洗涤使用超声波清洗机进行3-5小时。
-
公开(公告)号：KR102246258B1
公开(公告)日：2021-04-28
申请号：KR1020200005114
申请日：2020-01-15
Applicant: 목포대학교산학협력단
IPC: C04B35/505 , C04B35/626 , C04B35/632 , C04B35/64 , C01F17/218
Abstract: 본발명의나노이트리아소결체의제조방법은폴리머용액합성방법을이용하여비표면적이넓은나노아트리아분말을합성하고이를분산제의농도및 pH가최적화된수계의조건으로분산한후 압축성형또는슬립캐스팅방법으로성형체를제조하므로입자사이의기공이형성되지않아상압이며상대적으로저온인 1600 내지 1700℃인조건에서소결하여도치밀도가높으며투광성이우수한소결체를제조할수 있는장점이있다.
-
公开(公告)号：KR101808061B1
公开(公告)日：2017-12-12
申请号：KR1020160033405
申请日：2016-03-21
Applicant: 목포대학교산학협력단
Abstract: 본발명에서는하이드록시아파타이트또는제3인산칼슘등의인삼칼슘계물질을합성하기위하여열처리한난각을출발물질로사용하며, 난각과인산용액을혼합하는상온반응및 용액공정을이용하는한편, 인산용액의농도와 pH를변화시켜인삼칼슘의결정상과입자형태를제어한다. 높은표면적을가지는난각분말과인산용액을상온에서혼합하는과정에서격렬한발열반응이진행되며, 후속적인열처리로결정상을변화시켰다. 상온에서의모든반응물은 pH가 0.69인샘플을제외하고 Ca(PO)상을보였다. 40 wt% 농도의인산용액을사용한샘플은 800℃의열처리를통해성공적으로 HA를합성한반면, 60 wt% 농도의인산용액을사용한샘플은 1150℃의열처리에서 HA를생성하였다. pH 값이상온반응물및 열처리된샘플들의미세구조에큰 영향을미치며, 입자사이즈는용액의 pH 값에반비례하는것을확인하였다.
-
Patent Agency Ranking
公开(公告)号：KR1020170109371A
公开(公告)日：2017-09-29
申请号：KR1020160033405
申请日：2016-03-21
Applicant: 목포대학교산학협력단
Abstract: 본발명에서는하이드록시아파타이트또는제3인산칼슘등의인삼칼슘계물질을합성하기위하여열처리한난각을출발물질로사용하며, 난각과인산용액을혼합하는상온반응및 용액공정을이용하는한편, 인산용액의농도와 pH를변화시켜인삼칼슘의결정상과입자형태를제어한다. 높은표면적을가지는난각분말과인산용액을상온에서혼합하는과정에서격렬한발열반응이진행되며, 후속적인열처리로결정상을변화시켰다. 상온에서의모든반응물은 pH가 0.69인샘플을제외하고 Ca(PO)상을보였다. 40 wt% 농도의인산용액을사용한샘플은 800℃의열처리를통해성공적으로 HA를합성한반면, 60 wt% 농도의인산용액을사용한샘플은 1150℃의열처리에서 HA를생성하였다. pH 값이상온반응물및 열처리된샘플들의미세구조에큰 영향을미치며, 입자사이즈는용액의 pH 값에반비례하는것을확인하였다.
Abstract translation: 在本发明中，羟基磷灰石或3蛋壳热处理来合成人参钙类物质，如磷酸钙和用作起始材料，使用室温下反应，和蛋壳过磷酸钙溶液。另一方面，磷酸溶液的浓度进行混合的溶液步骤 并控制pH值来控制人参钙的构象和颗粒形状。 并且在室温下具有高的表面积的蛋壳粉末过磷酸钙溶液混合的过程中，放热反应的进行，通过随后的热处理改变到结晶相。 除pH值为0.69的样品外，所有反应物在室温下均显示出Ca（PO）相。 40克重量％的样品随着浓度的磷酸溶液中，同时成功地合成HA至800℃uiyeol治疗，使用60重量％浓度的磷酸溶液中的样品进行了在HA 1150℃uiyeol处理产生。 pH值显著影响反应温度和热处理后的样品的微观结构，该产品的粒径，确认为反比于该溶液的pH值。
-
公开(公告)号：KR101769742B1
公开(公告)日：2017-08-21
申请号：KR1020160067978
申请日：2016-06-01
Applicant: 목포대학교산학협력단
IPC: C23C4/11 , C23C4/00 , C04B35/626 , C23C24/08 , C04B35/18
CPC classification number: C23C24/08 , C04B35/18 , C04B35/6261 , C04B35/62625 , C04B35/62655
Abstract: 본발명은천연납석분말을용매에혼합하고분산제를첨가하여슬러리를제조하고, 상기슬러리를볼밀링하여납석분말을평균입도 1 ~ 4㎛의범위로분쇄하고, 상기슬러리를분무건조하여납석과립분말을제조하고, 상기납석과립분말을열처리하는단계를포함하는용사코팅용납석과립분말제조방법을제공한다.
-
公开(公告)号：KR1020140114732A
公开(公告)日：2014-09-29
申请号：KR1020130152382
申请日：2013-12-09
Applicant: 목포대학교산학협력단
Inventor： 이상진
CPC classification number: C09K11/7706 , B01J6/001 , C09K11/7774
Abstract: The present invention relates to a method for preparing a YAG:Ce3+ phosphor powder by solution synthesis using a PVA, and more particularly, to a method for fabricating a YAG:Ce3+ phosphor powder by solution synthesis using a PVA, the method being characterized in that a PVA solution is added to Y and Ce metal salt mixtures so that a ratio of atomic valence of PVA to atomic valence of metal cation is 2:1 to 20:1 (atomic valence of metal cation: atomic valence of PVA anion) and then, a precursor in a gel state is calcined and heat treated (sintered), the precursor obtained by adding Al2O3 seed powder to the mixed aqueous solution. According to the present invention, it is possible to synthesize a phosphor prepared at a low heat treatment temperature and a short retention time, having an equivalent level of light emission intensity to a conventional YAG phosphor without a milling process and a dispersant treatment process after drying and of which particle formation is controllable.
Abstract translation: 本发明涉及通过使用PVA的溶液合成制备YAG：Ce 3+荧光体粉末的方法，更具体地说，涉及通过使用PVA的溶液合成制造YAG：Ce 3+荧光体粉末的方法，其特征在于， 将PVA溶液加入到Y和Ce金属盐混合物中，使得PVA的原子价与金属阳离子的原子价的比例为2:1至20:1（金属阳离子的原子价：PVA阴离子的原子价），然后 ，将凝胶状态的前体煅烧并热处理（烧结），通过将Al 2 O 3种子粉末添加到混合水溶液中而获得的前体。 根据本发明，可以合成在低热处理温度和短停留时间制备的荧光体，其具有与传统的YAG荧光体相当的发光强度，而不需要研磨工艺和干燥后的分散剂处理工艺 并且其颗粒形成是可控的。
-
公开(公告)号：KR101412096B1
公开(公告)日：2014-06-26
申请号：KR1020120049695
申请日：2012-05-10
Applicant: 목포대학교산학협력단 , 한국농어촌공사
Abstract: 본 발명의 열처리소금 제조용 황토 용기는, 황토를 325 mesh를 통과한 1-40 μm 의 미세 입자의 황토를 얻는 단계; 상기 황토에 물과 삼성분계소지를 첨가하여 혼합하여 혼합물을 만드는 단계; 상기 혼합물을 균질화하여 슬러리를 만드는 단계; 상기한 슬러리를 (석고)몰드에 넣어 황토 용기를 성형한 다음 그늘에서 자연 건조하는 단계; 상기한 성형된 황토 용기를 섭씨 1200 내지 1400도에서 40 내지 80 분간 가열하는 단계를 포함하는 것을 특징으로 하며, 상기한 황토와 물은 그 혼합 비율이 1 : 1 중량비율인 것을 특징으로 하며, 상기한 황토와 삼성분계소지의 혼합 비율은, 황토 70-95중량%와 삼성분계소지 5-30중량% 비율인 것을 특징으로 하며, 상기한 성형되는 황토 용기는 원통 형상이며, 그 크기는 직경이 10-15센치미터, 높이가 10-14센치미너, 두께가 0.5 내지 1 센치미터인 것을 특징으로 한다.
본 발명에 의하여 제조된 열처리소금 제조용 황토 용기는 본 발명자가 종래 출원한 미네랄 죽염의 제조에 사용한 세라믹 용기에 비해 저비용으로 제조가 가능하고, 기존 황토 용기에서 문제가 되는 열처리소금의 손실이 거의 발생하지 않아 원료비 등의 제조비용을 절감하고 생산 효율을 높일 수 있는 할 수 있는 장점이 있다. 또한 본 발명에 따른 열처리소금 제조용 황토 용기로 본 발명자가 종래 출원한 미네랄 죽염의 제조 방법과 동일한 방법으로 제조된 미네랄죽염은 건강 기능성이 우수하다고 알려진 자색을 지닌 열처리소금(즉 자죽염)에 비해 미네랄이 풍부하고 기능성 가스신호전달물질인 황화수소를 생성하는 물질을 다량 함유하고 있다.-
公开(公告)号：KR102076789B1
公开(公告)日：2020-02-12
申请号：KR1020180074660
申请日：2018-06-28
Applicant: 목포대학교산학협력단 , 주식회사 대한
IPC: C09D7/61 , C09D5/18 , C09D201/00
-
-
-
-
-
-
-
-
-