公开(公告)号：KR101755283B1
公开(公告)日：2017-07-10
申请号：KR1020160004702
申请日：2016-01-14
Applicant: 한국화학연구원
Abstract: 본발명은루테튬, 알루미늄및 세륨원소의몰 비가 2.5 내지 2.95 : 5.3 내지 7.0 : 0.05 내지 0.5가되도록루테튬전구체, 알루미늄전구체및 세륨전구체를융제와혼합하여혼합물을준비하는단계(단계 1); 및상기단계 1에서준비된혼합물을환원열처리하여하기화학식 1로표시되는루테튬알루미늄가넷계형광체를제조하는단계(단계 2);를포함하는루테튬알루미늄가넷계형광체제조방법을제공한다. LuAlO:xCe(상기화학식 1에서, x는 0.05 ≤ x ≤ 0.5이고, y는 0.3 ≤ y ≤ 2.0이다.) 본발명에따른루테튬알루미늄가넷계형광체제조방법은루테튬및 세륨에대한알루미늄의비율을비화학양론적으로변화시킴으로써, 입도가제어된형광체는고출력의조명소자에적용가능하고, 향상된내열성을갖는장점이있다. 또한, 융제의종류및 함량조절을통해입도를조절할수 있는효과가있다.
Abstract translation: 本发明镥，铝和铈元素2.5至2.95的摩尔比：5.3至7.0：步骤（步骤1）制备镥前体，使得0.05〜0.5的混合物，铝前体和铈前体与助熔剂混合; 它提供了一个镥铝石榴石荧光材料的制造方法，包括;以及用于制备由下列通式（1）由在步骤1（步骤2）中制备的混合物的还原热处理表示的镥铝石榴石荧光材料的步骤。 <通式1> LuAlO：XCE（在式1中，x在0.05≤X≤0.5，y为0.3≤ÿ≤2.0），根据本发明的镥铝石榴石荧光材料的制造方法中铝为镥和铈 粒度受到控制的荧光体可以应用于高功率照明装置，具有耐热性提高的优点。 另外，可以通过调节助焊剂的种类和含量来控制粒度。
-
公开(公告)号：KR101678410B1
公开(公告)日：2016-11-23
申请号：KR1020140107696
申请日：2014-08-19
Applicant: 한국화학연구원
IPC: H01M4/139 , H01M4/38 , H01M4/62 , H01M4/1395 , H01M10/052
Abstract: 본발명은리튬이차전지용전극및 이의제조방법에관한것으로, 보다상세하게는 2차원형태의전도성소재와구형또는 1차원형태의나노금속소재및 활성소재의단순혼합만으로소재간의혼성화가가능하고, 이를통하여, 전도성소재-나노금속소재-활성소재간의 3차원네트워킹을형성함으로써, 고용량을가지면서반복충방전특성이우수한리튬이차전지용전극및 이의제조방법에관한것이다.
-
公开(公告)号：KR1020160008259A
公开(公告)日：2016-01-22
申请号：KR1020140088107
申请日：2014-07-14
Applicant: 한국화학연구원
Abstract: 본발명은이종금속복합체의제조방법및 이를이용한전극에관한것으로, 보다구체적으로는다양한전도성물질을이용함으로서, 금속산화물전구체또는금속산화물의표면전위를조절함으로서, 용이하게이종금속복합체를제조할수 있는방법을제공하는것이며, 이를이용한전극은전기화학적특성이우수하여, 이는전극재료로서하이브리드형전지에유용하게사용될수 있다.
Abstract translation: 本发明涉及一种生产不同种类的金属的复合材料的方法和使用它们制造的电极。 通过使用各种导电材料调节金属氧化物的前体的表面电位或金属氧化物的表面电位，可以容易地制造不同种类的金属的复合物。 通过使用不同种类的金属的复合体制造的电极具有优异的电化学性能，并且可以有利地用作混合型电池的电极材料。
-
公开(公告)号：KR101468582B1
公开(公告)日：2014-12-03
申请号：KR1020130014537
申请日：2013-02-08
Applicant: 한국화학연구원
IPC: H01M4/1395 , H01M4/58 , H01M10/02
Abstract: 본발명은다공성실리카지지체를이용한전극활물질의제조방법및 이에따라제조되는전극활물질에관한것으로, 상세하게는리튬전구체, 망간전구체, 킬레이트제, 중합조제, 및환원제를용매에첨가하고혼합하는단계(단계 1); 상기단계 1의혼합물에다공성실리카지지체를첨가및 혼합하여반응시키는단계(단계 2); 및상기단계 2의반응물을환원분위기에서열처리하는단계(단계 3)를포함하는다공성실리카지지체를이용한전극활물질의제조방법을제공한다. 본발명에따른제조방법은전극활물질로서사용될수 있는규산염계망간리튬화합물을제조할수 있다. 이때, 본발명에따라제조된규산염계망간리튬화합물은전극활물질로이용되는경우, 기존의일반적인실리카재료를사용하여제작된규산염계망간리튬화합물과비교하여초기용량면에서우수한특성을나타내는효과가있다. 또한, 본발명에따라제조된규산염계망간리튬화합물은카본코팅, 이종원소도핑, 볼밀등의후처리공정이필요하지않기때문에저비용으로리튬이차전지전극활물질을제조할수 있는장점이있다.
Abstract translation: 本发明涉及使用多孔二氧化硅载体的电极活性物质及其制造的电极活性物质的制造方法。 具体而言，本发明提供使用多孔二氧化硅载体的电极活性物质的制造方法，其包括在溶剂中添加锂前体，锰前体，螯合剂，聚合剂和还原剂的工序，以及 混合（步骤1）; 在步骤1的混合物中加入和混合多孔二氧化硅载体并反应（步骤2）的步骤; 以及在还原条件下热处理步骤2的产物的步骤。 根据本发明的制造方法可以制造可用作电极活性材料的硅酸盐基锰锂化合物。 当将根据本发明制造的硅酸盐基锰锂化合物用作电极活性材料时，与通过使用现有的一般化合物制造的硅酸盐基锰锂化合物相比，具有优异的初始容量性能 二氧化硅材料。 此外，根据本发明制造的硅酸盐基锰锂化合物不需要诸如碳涂覆，异质元素掺杂，球磨等的后处理工艺，并且因此提供能够制造电极活性的优点 锂二次电池的材料成本低。
-
公开(公告)号：KR101434459B1
公开(公告)日：2014-08-26
申请号：KR1020130098581
申请日：2013-08-20
Applicant: 한국화학연구원
Abstract: The present invention relates to a novel bromosilicate-based phosphor for near-ultraviolet excitation, a method of preparing the same, and a light-emitting device using the same. Particularly, the present invention relates to (Ca_3_-x,Eu_x)SiO_4Br_2 phosphor, (Ca_3-x-yMg_yEu_x)SiO_4Br_2 phosphor, (Ca_3_-x-_yMg_yEu_x_)SiO_4(Br_2_-_zD_z) phosphor, a method of preparing the same, and a light-emitting device using the same. The phosphor according to the present invention absorbs lights in 250-450 nm in a near-ultraviolet region having high excitation efficiency, emits lights in 450-750 nm in a whole visible region, and exhibits high emission luminance, and may be usefully used as a phosphor of a light-emitting device for near-ultraviolet excitation. Particularly, the phosphor of the present invention may be usefully used as a phosphor of a white emitting diode for near-ultraviolet excitation.
Abstract translation: 本发明涉及一种用于近紫外激发的新型溴硅酸盐系荧光体及其制备方法以及使用其的发光装置。 特别地，本发明涉及（Ca_3_-x，Eu_x）SiO_4Br_2荧光体，（Ca_3-x-yMg_yEu_x）SiO_4Br_2荧光体，（Ca_3_-x-_yMg_yEu_x_）SiO_4（Br_2_-zD_z）荧光粉，其制备方法， 使用该发光装置的发光装置。 根据本发明的荧光体在具有高激发效率的近紫外区域中吸收250-450nm的光，在整个可见光区域发射450-750nm的光，并且显示高的发光亮度，并且可以有效地用作 用于近紫外激发的发光装置的荧光体。 特别地，本发明的荧光体可以有用地用作用于近紫外激发的白色发光二极管的荧光体。
-
Patent Agency Ranking
公开(公告)号：KR1020140101183A
公开(公告)日：2014-08-19
申请号：KR1020130014537
申请日：2013-02-08
Applicant: 한국화학연구원
IPC: H01M4/1395 , H01M4/58 , H01M10/02
CPC classification number: C01B33/20 , C01P2006/40 , H01M4/48 , H01M4/505 , H01M10/052 , Y02E60/12
Abstract: The present invention relates to a manufacturing method of an electrode active material using a porous silica support and an electrode active material manufactured thereby. Specifically, the present invention provides a manufacturing method of an electrode active material using a porous silica support, which comprises a step of adding a lithium precursor, a manganese precursor, a chelating agent, a polymerizing agent and an reducing agent in a solvent, and mixing (step 1); a step of adding and mixing a porous silica support in the mixture of step 1, and reacting (step 2); and a step of thermally processing the product of step 2 in a reduction condition. The manufacturing method according to the present invention can manufacture a silicate-based manganese lithium compound, which can be used as an electrode active material. When the silicate-based manganese lithium compound manufactured according to the present invention is used as an electrode active material, it has an effect of showing an excellent property in the initial capacity in comparison with the silicate-based manganese lithium compound manufactured by using existing general silica materials. Also, the silicate-based manganese lithium compound manufactured according to the present invention does not require post-treatment processes such as carbon coating, hetero-element doping, ball milling, etc., and, therefore, providing advantages capable of manufacturing an electrode active material for a lithium secondary battery at low costs.
Abstract translation: 本发明涉及使用多孔二氧化硅载体的电极活性物质及其制造的电极活性物质的制造方法。 具体而言，本发明提供使用多孔二氧化硅载体的电极活性物质的制造方法，其包括在溶剂中添加锂前体，锰前体，螯合剂，聚合剂和还原剂的工序，以及 混合（步骤1）; 在步骤1的混合物中加入和混合多孔二氧化硅载体并反应（步骤2）的步骤; 以及在还原条件下热处理步骤2的产物的步骤。 根据本发明的制造方法可以制造可用作电极活性材料的硅酸盐基锰锂化合物。 当将根据本发明制造的硅酸盐基锰锂化合物用作电极活性材料时，与通过使用现有的一般化合物制造的硅酸盐基锰锂化合物相比，具有优异的初始容量性能 二氧化硅材料。 此外，根据本发明制造的硅酸盐基锰锂化合物不需要诸如碳涂覆，异质元素掺杂，球磨等的后处理工艺，并且因此提供能够制造电极活性的优点 锂二次电池的材料成本低。
-
公开(公告)号：KR101164035B1
公开(公告)日：2012-07-18
申请号：KR1020090111514
申请日：2009-11-18
Applicant: 한국화학연구원
Abstract: 본 발명은 가시광 영역에서 투과도가 우수한 아연/망간 실리케이트계 투명 녹색 형광막의 제조 방법에 관한 것으로서, 보다 상세하게 설명을 하면, 서브마이크론(submicron) 이하의 입자크기를 갖는 구형 실리카를 제조한 후, 이를 아연 전구체와 망간 전구체 등을 포함하는 수용액에 첨가하여 제조한 아연/망간 실리케이트 겔을 소성하여 녹색의 형광체를 제조하거나 또는 상기 아연/망간 실리케이트 겔을 용액코팅하여 투명 녹색 형광막을 제조하는 방법에 관한 것이다. 본 발명의 제조방법으로 제조된 투명 녹색 형광막은 발광 특성 및 분산 특성이 우수하고, 가시광 영역에서 투과도가 우수하기 때문에, 투명 디스플레이 소자에 사용하기에 적합하다. 또한, 기존의 진공증착 시스템을 이용하여 제조한 박막형 형광막에 비교하여 발광효율 및 투광성이 높을 뿐만 아니라, 적색에서부터 청색까지 다양한 발광색을 변화시킬 수 있어서, 백색 디스플레이를 구현할 수 있다.
형광입자, 형광막, 코어-쉘, 스핀코팅, 발광, 아연/망간 실리케이트-
公开(公告)号：KR1020120072548A
公开(公告)日：2012-07-04
申请号：KR1020100134342
申请日：2010-12-24
Applicant: 한국화학연구원
Abstract: PURPOSE: A calcium silicophosphate-based green electroluminescent phosphor is provided to be excited by an excitation light source of 250-450 nm, thereby imparting excellent luminescent brightness, and color purity. CONSTITUTION: A manufacturing method of calcium silicophosphate-based green electroluminescent phosphor comprises: a step of manufacturing a precursor mixture by weighing calcium precursor, silicon precursor, phosphorous precursor, and europium precursor within the content range of chemical formula 1: Ca_(7-x)(SiO_4)_2(PO_4)_2:xEu (0
Abstract translation: 目的：提供一种基于硅磷酸钙的绿色电致发光荧光体，由250-450nm的激发光源激发，从而赋予发光亮度优异和色纯度。 构成：基于硅磷酸钙的绿色电致发光荧光体的制造方法包括：通过在化学式1的含量范围内称量钙前体，硅前体，磷前体和铕前体制备前体混合物的步骤：Ca（7-x ）（SiO_4）_2（PO_4）_2：xEu（0
-
公开(公告)号：KR101026533B1
公开(公告)日：2011-04-01
申请号：KR1020090023603
申请日：2009-03-19
Applicant: 한국화학연구원
IPC: C09K11/78
Abstract: 본 발명은 신규한 자외선 여기용 적색 형광체로서, 더욱 상세하게는 바륨, 이트륨산화물을 함유하여 이루어진 모체와, 유로퓸을 활성원소로 이용하고 마그네슘을 첨가 이온으로 사용한 적색 형광체에 관한 것이다.
본 발명에 따른 적색 형광체는 250 ~ 300 nm 범위의 자외선 영역에서 높은 흡수 피크를 나타내고 우수한 색순도 특성 및 화학적으로 안정한 산화물을 기반으로한 조성물로서 고효율 적색 발광 물질로의 적용이 가능하다.
적색형광체, 자외선, 바륨, 이트륨, 유로퓸, 마그네슘-
公开(公告)号：KR100907090B1
公开(公告)日：2009-07-09
申请号：KR1020070137552
申请日：2007-12-26
Applicant: 한국화학연구원
IPC: C09K11/55
Abstract: 본 발명은 칼슘, 스트론튬, 바나듐 원소를 함유하여 이루어진 모체와, 유로퓸을 활성원소로 함유하는 적색형광체로, 250 nm 이상의 장파장 자외선 영역에서 높은 발광 효율을 나타내므로 자외선 여기 발광 다이오드를 여기 에너지원으로 사용 시 유용한 바나데이트계 적색형광체와 이의 제조방법에 관한 것이다.
적색 형광체, 장파장 자외선 여기용, 바나데이트
-
-
-
-
-
-
-
-
-