公开(公告)号：KR1019950010548B1

公开(公告)日：1995-09-19

申请号：KR1019920021497

申请日：1992-11-16

Applicant: 제일모직주식회사

Inventor： 정필문 ,  정하식 ,  박현길

IPC: C08F2/24 ,  C08F279/00

Abstract: The rubbric latex is prepd. by emulsion polymerization of 70-100 wt.pts. of a conjugated dien type monomer, and/or 30-0 wt.pts. of a vinyl type monomer, 60-150 wt.pts. of an ion exchanging water, and 0.5-10.0 wt.pts. of an emulsifying agent, where a part of the emulsifying agent is added at an early step and the remainder of the emulsifying agent is continueosly added in the reaction. The conjugated dien type monomer is the mixt. comprising one or more of 1,3-butadien, isoprene, 2,3-dimethyl-1,3-butadien, 2-chlorobutadien-1 ! ,3, or 2,3-dichlorobutadien-1,3; and the vinyl type monomer is styrene, vinyl toluene, divinyl benzene, or alpha-methyl styrene.

Abstract translation: 乳胶乳是制备的。 通过70-100重量ppm的乳液聚合。 的共轭二烯型单体，和/或30-0wt.pts。 的乙烯基类单体，60-150重量份。 的离子交换水，和0.5-10.0重量ppm。 的乳化剂，其中一部分乳化剂在早期步骤中加入，剩余的乳化剂在反应中继续加入。 共轭二烯型单体是混合物。 包括一种或多种1,3-丁二烯，异戊二烯，2,3-二甲基-1,3-丁二烯，2-氯丁二烯-1 ，3或2,3-二氯丁二烯-1,3; 乙烯基类单体是苯乙烯，乙烯基甲苯，二乙烯基苯或α-甲基苯乙烯。

公开(公告)号：KR1019950011490A

公开(公告)日：1995-05-15

申请号：KR1019930022061

申请日：1993-10-22

Applicant: 제일모직주식회사

Inventor： 정하식 ,  정필문 ,  하두한

IPC: C08F279/00

Abstract: 본 발명은 열가소성 수지의 제조방법에 관한 것이다.
본 발명은 내충격성 및 유동성을 그대로 유지하면서 광택도와 백색도가 우수한 열가소성 수지를 제공하는데 목적이 있다.
본 발명은 1) 평균입도 0.25 - 0.32 마이크로, 겔함유량이 70 - 85중량%의 부타디엔 고무라텍스 중합체 30 - 65 중량부와,
2) 상기 공중합체에 2 단계 그라프트 중합을 행하는에 있어 스티렌 18.37 - 9.18중량부, 아크릴로니트릴 6.13 - 3.07 중량부의 단량체혼합물, 유화제, 분자량조절제, 텍스트로우스, 중합개시제 및 이온교환수 첨가후 승온하여 레독스계 산화환원 촉매인 황산제일철 및 피로인산나트륨을 각각 0.001 - 0.35 중량부를 첨가하여 1차 그라프트 시키는 1단계 반응과,
3) 상기 1차 그라프트 라텍스에 스티렌 34.12 - 17.06 중량부, 아크릴로니트릴 11.38 - 5.69 중량부의 단량체혼합물, 유화제, 분자량조절제 및 이온교환수를 프리에멀젼 상태로 만든후 1시간에서 4시간 걸쳐 연속 투입하는 2단계반응으로 구성되며,
4) 상기 2단계 반응에 있어서, 단량체의 연속투입시 나트륨포륨알데히드술폭실레이트, 에틸렌디아민트리아세트산, 황산제일철을 각각 0.0005 - 0.25 중량부를 첨가하는 하며,
5) 상기 2단계 반응에 있어서, 단량체의 연속 투입시 중합 개시제인 큐멘하이드록퍼옥사이드를 1시간에서 4시간 걸쳐 연속적으로 투입하는 것을 특징으로 한다.