公开(公告)号：KR1020080063226A
公开(公告)日：2008-07-03
申请号：KR1020070141890
申请日：2007-12-31
Applicant: 고려대학교 산학협력단
Abstract: A method for preparing a PTFE coating solution is provided to reduce the frictional coefficient of a PTFE coating layer, the bad effect due to heat and specific wear rate, thereby improving the lifetime of a PTFE coating layer. A method for preparing a PTFE coating solution comprises the steps of adding an organic solvent and a carbon nanoparticle to a container containing a bead to mix them and adding an impeller to seal it; rotating the impeller with a velocity of 1,000-3,000 rpm to pulverize it to obtain a carbon nanoparticle organic dispersion having an average diameter of 300-1,000 nm; and separating the organic dispersion from the bead and the container and mixing it with a nonaqueous PTFE solution containing PTFE and NMP to prepare a PTFE coating solution having a sintering temperature of 200-250 deg.C.
Abstract translation: 提供一种制备PTFE涂布溶液的方法，以降低PTFE涂层的摩擦系数，由于热和比磨损速率引起的不良影响，从而提高PTFE涂层的使用寿命。 制备PTFE涂布溶液的方法包括以下步骤：将有机溶剂和碳纳米颗粒加入到含有珠粒的容器中以混合它们并加入叶轮以密封它; 以1,000-3,000rpm的速度旋转叶轮以粉碎，得到平均直径为300-1,000nm的碳纳米颗粒有机分散体; 从珠粒和容器中分离有机分散体，并与含有PTFE和NMP的非水PTFE溶液混合，制备烧结温度为200-250℃的PTFE涂布溶液。
-
公开(公告)号：KR100946403B1
公开(公告)日：2010-03-09
申请号：KR1020070141890
申请日：2007-12-31
Applicant: 고려대학교 산학협력단
Abstract: PTFE 코팅용액의 제조방법이 제공된다.
본 발명에 따른 PTFE 코팅용액의 제조방법은 (a) 비이드가 담긴 용기에 유기용매와 나노 카본 분말을 혼합한 후, 임펠러를 넣고 밀봉하는 단계; (b) 상기 임펠러를 1000∼3000rpm의 속도로 회전시키며 60∼175분 동안 분쇄하여 평균입도가 300∼1000nm인 나노 카본 입자 유기분산액을 얻는 단계; 및 (c) 상기 유기분산액을 비이드와 용기로부터 분리하고 NMP를 함유하는 비수성 PTFE 용액과 혼합하여 소성온도가 200∼250℃인 PTFE 코팅용액을 제조하는 단계를 포함하는 것을 특징으로 하며, PTFE 코팅층의 마찰계수를 낮출 수 있을 뿐만 아니라, 코팅 모재에 열에 의한 악영향을 감소시킬 수 있고, 무엇보다도 비마모율을 현저히 낮출 수 있기 때문에 PTFE 코팅층의 수명을 대폭 향상시킬 수 있다.-
公开(公告)号：KR100896340B1
公开(公告)日：2009-05-07
申请号：KR1020060044726
申请日：2006-05-18
Applicant: 고려대학교 산학협력단
Abstract: 양파모양탄소입자 분산액의 제조방법이 개시된다.
본 발명은 나노다이아몬드입자를 불활성기체분위기에서 가열하여 4 내지 10㎚의 1차결정을 가진 양파모양탄소입자를 준비하는 단계;
증류수에 상기 양파모양탄소입자 0.2 내지 10 중량%와 음이온성분산제 0.2 내지 5 중량%를 적하하고, 염기시약을 첨가하여 pH 8.5 이상을 유지하는 혼합용액을 만드는 단계;
상기 혼합용액을 밀폐된 교반기에 투입하되, 상기 교반기내부의 전체 100 부피%를 기준으로 상기 혼합용액 30 내지 50 부피%와 교반입자 50 내지 70 부피%를 투입하여 교반하는 단계; 및
상기 교반입자를 혼합용액에서 분리하여 양파모양탄소입자가 분산된 혼합용액을 수득하는 단계;를 포함하는 것을 특징으로 하는 양파모양탄소입자 분산액의 제조방법에 관한 것으로서, 윤활성과 같은 기계적 물성이 우수한 미세한 크기의 양파모양탄소입자를 수용액상으로 제공하고, 더욱이 수용액상에서 2차 응집되지 않는 분산성이 우수한 특징이 있다.-
公开(公告)号：KR1020070111654A
公开(公告)日：2007-11-22
申请号：KR1020060044726
申请日：2006-05-18
Applicant: 고려대학교 산학협력단
Abstract: A method for preparing a dispersion of onion-like carbon particles is provided to obtain an aqueous solution of onion-like carbon particles having excellent mechanical properties such as lubricating property and a fine particle size and showing excellent dispersibility sufficient for preventing secondary agglomeration. A method for preparing a dispersion of onion-like carbon particles comprises: a step(S1) of heating diamond nanoparticles under an inert gas atmosphere to provide onion-like carbon particles containing primary crystals having a size of 4-10nm; a step(S2) of adding dropwise 0.2-10 wt of the onion-like carbon particles and 0.2-5 wt% of an anionic dispersant to distilled water, and further adding a base reagent to form a mixed solution maintaining a pH of 8.5 or higher; a step(S3) of introducing the mixed solution into a sealed agitator in an amount of 30-50 vol% based on the total volume of the agitator along with 40-70 vol% of agitation particles; and a step(S4) of separating the agitation particles from the mixed solution to obtain a mixed solution in which the onion-like carbon particles are dispersed. The anionic dispersant is selected from a group consisting of sodium dodecylsulfonate, calcium dodecylsulfonate, polyacrylic acid, 1,2,3,4-butanetetracarboxylic acid.
Abstract translation: 提供了制备洋葱状碳颗粒分散体的方法，以获得具有优异的机械性能如润滑性能和细粒度的洋葱状碳颗粒水溶液，并显示出足以防止二次凝聚的优异分散性。 制备洋葱状碳颗粒分散体的方法包括：在惰性气体气氛下加热金刚石纳米颗粒以提供含有4-10nm尺寸的初晶的洋葱状碳颗粒的步骤（S1）; 向蒸馏水中滴加0.2-10重量的洋葱状碳粒子和0.2〜5重量％的阴离子性分散剂的步骤（S2），进一步添加碱试剂以形成维持pH为8.5的混合溶液或 更高; 基于搅拌器的总体积和40-70体积％的搅拌颗粒，将混合溶液以30-50体积％的量引入密封搅拌器的步骤（S3） 以及从混合溶液中分离搅拌粒子的步骤（S4），得到分散有洋葱状碳粒子的混合溶液。 阴离子分散剂选自十二烷基磺酸钠，十二烷基磺酸钙，聚丙烯酸，1,2,3,4-丁烷四羧酸。
-
-
-