Abstract: An epoxy resin curable composition suggested in the present invention comprises cycloaliphatic epoxy resin, an aromatic diamine curable agent and a strong acid salt catalyst. The epoxy resin curable composition has 500 to 1,500 cps of viscosity of a mixture at room temperature, equal to or higher than 1.8% of tensile elongation after hardening, and equal to or higher than 200°C of glass transition temperature. According to the present invention, resins can be mass-produced, which can be applied to a process for filament winding or the like because of having excellent heat resistance while having lower viscosity than an epoxy resin curable composition with the existing heat resistance.

Abstract translation: 本发明中提出的环氧树脂可固化组合物包括脂环族环氧树脂，芳族二胺可固化剂和强酸盐催化剂。 环氧树脂固化性组合物在室温下的粘度为500〜1500cps，硬化后的拉伸伸长率为1.8％以上，玻璃化转变温度为200℃以上。 根据本发明，由于与具有现有耐热性的环氧树脂固化性组合物相比具有较低粘度的耐热性优异，因此可以批量生产树脂，其可应用于丝缠绕等方法。

公开(公告)号：KR101485390B1

公开(公告)日：2015-01-26

申请号：KR1020130033743

申请日：2013-03-28

Applicant: 국방과학연구소

Inventor： 정상기 ,  김민영 ,  안치운 ,  박영제

IPC: C08G59/18 ,  C08G59/50 ,  C08L63/00 ,  C08K5/17

Abstract: 본 발명에서 제시하는 에폭시 수지 경화 조성물은 사이클로알리파틱계 에폭시 수지, 방향족 디아민 경화제, 및 강산염 촉매를 포함한다. 에폭시 수지 경화 조성물은 혼합물의 점도가 상온에서 500~1,500cps, 경화 후 인장신율이 1.8% 이상, 유리전이온도가 200℃ 이상이다. 본 발명에 의하면, 기존의 내열성을 가지는 에폭시 수지 경화 조성물보다 점도가 낮으면서 내열도가 우수하여 필라멘트 와인딩 등의 공정에 적용할 수 있는 수지를 양산할 수 있다.

Abstract translation: 本发明提出的环氧树脂固化组合物包括脂环族环氧树脂，芳族二胺固化剂和强酸盐催化剂。 环氧树脂固化用组合物的室温粘度为500〜1,500cps，固化后的拉伸伸长率为1.8％以上，玻璃化转变温度为200℃以上。 根据本发明，可以制造比具有耐热性的常规环氧树脂固化组合物低的粘度和耐热性的树脂，并且可以应用于例如长丝卷绕的过程。