公开(公告)号：WO2016007990A1

公开(公告)日：2016-01-21

申请号：PCT/AU2015/000409

申请日：2015-07-13

Applicant: QENOS PTY LTD

Inventor： ADETUNJI, Philip ,  NAEBE, Minoo ,  EGAN, Brian ,  MICIC, Predrag ,  FOX, Bronwyn, Louise

IPC: C08K3/04 ,  F16L9/12 ,  C08L23/04

CPC classification number: C08K3/04 ,  B82Y30/00 ,  C08J3/203 ,  C08J2323/06 ,  C08K3/042 ,  C08K2201/011 ,  F16L9/12 ,  C08L23/04

Abstract: A polyethylene nanocomposite composition comprising: (i) base polyethylene resin of medium density polyethylene or high density polyethylene resin having a melt flow index in the range of from 0.10 to 1.4 g/10 min at 190° C and 5 kg as measured according to ISO 1133, high load melt flow index of from 4 to 20 g/10 min at 190° C and 21.6 kg as measured according to ISO 1133 and a density in the range of from about 0.930 to about 0.970 g/cm 3 at 23°C as measured according to ASTM D792; and (ii) planar carbon nanoparticles having a BET (from Brunauer-Emmett-Teller (BET) theory) surface area of at least 50 m 2 /g, in an amount of from 0.1% to 20% by weight based on the weight of the polyethylene nanocomposite composition.

Abstract translation: 一种聚乙烯纳米复合材料组合物，其包含：（i）中等密度聚乙烯或高密度聚乙烯树脂的基础聚乙烯树脂，其熔体流动指数在190℃下为0.10-1.4g / 10min，根据ISO测量为5kg 1133，根据ISO 1133测量，在190℃和21.6kg下的高负荷熔体流动指数为4至20g / 10min，在23℃下的密度在约0.930至约0.970g / cm 3的范围内，作为 根据ASTM D792测量; 和（ii）具有BET（来自Brunauer-Emmett-Teller（BET）理论））的表面积为至少50m 2 / g的平面碳纳米颗粒，其量为0.1重量％至20重量％，基于 聚乙烯纳米复合材料组合物。

公开(公告)号：EP3169727A1

公开(公告)日：2017-05-24

申请号：EP15822441.0

申请日：2015-07-13

Applicant: Qenos Pty Ltd.

Inventor： ADETUNJI, Philip ,  NAEBE, Minoo ,  EGAN, Brian ,  MICIC, Predrag ,  FOX, Bronwyn, Louise

IPC: C08K3/04 ,  F16L9/12 ,  C08L23/04

CPC classification number: C08K3/04 ,  B82Y30/00 ,  C08J3/203 ,  C08J2323/06 ,  C08K3/042 ,  C08K2201/011 ,  F16L9/12 ,  C08L23/04

Abstract: A polyethylene nanocomposite composition comprising: (i) base polyethylene resin of medium density polyethylene or high density polyethylene resin having a melt flow index in the range of from 0.10 to 1.4 g/10 min at 190° C. and 5 kg as measured according to ISO 1133, high load melt flow index of from 4 to 20 g/10 min at 190° C. and 21.6 kg as measured according to ISO 1133 and a density in the range of from about 0.930 to about 0.970 g/cm3 at 23° C. as measured according to ASTM D792; and (ii) planar carbon nanoparticles having a BET (from Brunauer-Emmett-Teller (BET) theory) surface area of at least 50 m2/g, in an amount of from 0.1% to 20% by weight based on the weight of the polyethylene nanocomposite composition.

Abstract translation: 一种聚乙烯纳米复合材料组合物，其包含：（i）中等密度聚乙烯或高密度聚乙烯树脂的基础聚乙烯树脂，其具有根据ISO测量的在190℃和5kg下为0.10-1.4g / 10min范围内的熔体流动指数 1133，在190℃和21.6kg下根据ISO 1133测量的4-20g / 10min的高负荷熔体流动指数和在23℃下的密度在约0.930-约0.970g / cm 3范围内 根据ASTM D792测量; 和（ii）具有至少50m 2 / g的BET（来自Brunauer-Emmett-Teller（BET）理论）表面积为0.1重量％至20重量％的平面碳纳米颗粒，基于 聚乙烯纳米复合材料组合物。