公开(公告)号：US4724078A

公开(公告)日：1988-02-09

申请号：US744458

申请日：1985-06-10

Applicant: Alain Auriol ,  Jacques Gillot

Inventor： Alain Auriol ,  Jacques Gillot

IPC: B01D39/20 ,  B01D71/02 ,  C04B38/00

CPC classification number: B01D71/024 ,  B01D39/2075 ,  B01D71/025 ,  C04B35/111 ,  C04B35/62665 ,  C04B38/00 ,  C04B2111/00612 ,  C04B2111/00793 ,  C04B2201/00 ,  C04B2235/5436 ,  C04B2235/5472 ,  C04B2235/6021 ,  C04B2235/94 ,  C04B2235/96

Abstract: A porous material made from sintered inorganic particles. It has an open pososity of 30% to 40% by volume, a permeability to water at 20.degree. ranging from 0.6 to 60 m.sup.3 /h.m.sup.2.bar for a wall thickness of 2 cm as the average pore diameter varies from 2 to 20 microns and a crushing resistance, measured under conditions of isostatic compression, of 4.times.10.sup.8 to 5.times.10.sup.8 N/m.sup.2.

Abstract translation: PCT No.PCT / FR84 / 00235 Sec。 371日期：1985年6月10日 102（e）1985年6月10日PCT PCT日期：1984年10月18日PCT公布。 第WO85 / 01937号公报 日期1985年5月9日。由烧结无机颗粒制成的多孔材料。 它具有30％至40体积％的开放的浓度，在20℃的水的渗透性为0.6至60m 3 / h.m2.bar，壁厚为2cm，平均孔径为2至20 在等静压压缩条件下测得的抗破碎性为4×10 8至5×10 8 N / m 2。

公开(公告)号：US4356215A

公开(公告)日：1982-10-26

申请号：US497953

申请日：1974-08-15

Applicant: Alain Auriol ,  Paul Tritten

Inventor： Alain Auriol ,  Paul Tritten

IPC: B01D35/00 ,  B01D39/14 ,  B01D39/20 ,  B01D53/00 ,  B01D59/12 ,  B01D59/14 ,  B01D71/02 ,  B05D5/00 ,  C04B41/50

CPC classification number: B01D67/0046 ,  B01D39/2075 ,  B01D59/12 ,  B01D69/088 ,  B01D69/10 ,  B01D69/12 ,  B01D71/02 ,  B01D71/025 ,  C04B41/009 ,  C04B41/5022 ,  B01D2323/08 ,  B01D67/0083

Abstract: The invention relates to a method of manufacturing supports for porous filters.Supports are placed in contact with a first slip coating liquid containing in suspension a mineral powder comprising agglomerates between 10 and 30 microns in diameter, the resulting deposited layer is dried by heating it to approximately 100.degree. C., the layer is brushed so as to remove particles of powder which have not penetrated inside the pores, the thus-treated supports are placed in contact with a second slip coating liquid containing in suspension a mineral powder having a particle size between 1 and 8 microns, and the products obtained are heat-treated at approximately 1500.degree. C.The resulting filters are used for separating isotopes.

Abstract translation: 本发明涉及一种制造多孔过滤器支撑件的方法。 将支撑体与包含悬浮液的第一滑移涂料液体接触，包含直径在10至30微米之间的附聚物的矿物粉末，所得沉积层通过加热至约100℃而干燥，以使其刷 除去未渗透到孔内的粉末颗粒，将如此处理的载体与悬浮液中含有粒度为1至8微米的矿物粉末的第二滑移涂料液接触， 在约1500℃下处理。所得到的过滤器用于分离同位素。

公开(公告)号：US4031177A

公开(公告)日：1977-06-21

申请号：US623274

申请日：1975-10-17

Applicant: Alain Auriol ,  Paul Tritten

Inventor： Alain Auriol ,  Paul Tritten

IPC: C04B35/115 ,  C04B35/64 ,  F27B9/04 ,  F27D7/06

CPC classification number: C04B35/64 ,  C04B35/115 ,  Y10S264/91

Abstract: Final sintering of an alumina powder containing a small portion of magnesia, baryta, lanthana, yttria, or salts of magnesium, barium, lanthanum or yttrium, in a non-oxidizing carbon monoxide atmosphere at a temperature above 1700.degree. C produces a translucent alumina article.

Abstract translation: 在非氧化性一氧化碳气氛中，在1700℃以上的温度下，含有少量氧化镁，重晶石，氧化镧，氧化钇或镁，钡，镧或钇的盐的氧化铝粉末的最终烧结产生半透明的氧化铝制品 。