A method for manufacturing of ultrahigh molecular weight polyethylene (UHMWPE) for implants, where the implants have been machined out of UHMWPE blocks or extruded rods, has anthocyanin dispersely imbedded in the polyethylene. The implant is then exposed to γ ray or electron beam irradiation in an amount of at least 2.5 Mrad followed by a heat treatment to prevent the implant from becoming brittle in the long term as well as to improve strength and wear. The method includes mixing a powder or granulate resin of UHMWPE with an aqueous liquid that contains anthocyanin in a predetermined amount. The water is then evaporated to deposit the anthocyanin in a predetermined concentration on the polyethylene particles. The doped UHMWPE particles are compressed into blocks at temperatures in a range of approximately 135° C.-250° C. and pressures in a range of approximately 2-70 MPa. Medical implants are made from the blocks.