公开(公告)号：KR1020040090125A
公开(公告)日：2004-10-22
申请号：KR1020030024053
申请日：2003-04-16
Applicant: 한국화학연구원 , 여수대학교산학협력단
CPC classification number: C08J5/005
Abstract: PURPOSE: A method for preparing a polymer-layered organic compound nanocomposite is provided to improve the production yield of crystalline silicate while reducing the production cost, and to control the interlayer distance in more economic and easier way, thereby expanding the interlayer distance and improving physical properties. Further, since the method uses only non-toxic organic solvent which is recycled in the method, pollutants are not generated, thereby being environmentally friendly. CONSTITUTION: The method for preparing a polymer-layered organic compound nanocomposite comprises: (1) preparing silica slurry by neutralizing sodium metasilicate(Na2SiO3) or fluorosilicic acid (H2SiF6) as silica sources while maintaining the conditions of a temperature of 20-80deg.C and a pH value of 6-12; (2) adding alkali to the prepared silica slurry so as to make the ratio of silica to alkali to the range of 1-25 to 1, the ratio of water to alkali to the range of 50-500 to 1, and carrying out a hydrothermal reaction of the mixture at 100-200deg.C for 1-200hours to prepare layered inorganic compounds of magadiite or kenyaite; (3) acidifying the layered inorganic compounds to form silanol groups between the layers, dispersing it to an organic solvent where a compound being possible to form a hydrogen bond with the silanol group is dissolved, and drying the resulted product by evaporation to obtain a layered organic compound; and (4) inserting a functional polymer between the layers of the layered organic compound.
Abstract translation: 目的：提供一种制备聚合物层状有机化合物纳米复合材料的方法，以提高结晶硅酸盐的生产成本，同时降低生产成本，并以更经济，更简单的方式控制层间距离，从而扩大层间距离，改善物理性能 属性。 此外，由于该方法仅使用在该方法中再循环的无毒有机溶剂，因此不会产生污染物，因此是环境友好的。 构成：制备聚合物层状有机化合物纳米复合材料的方法包括：（1）通过中和硅酸钠（Na2SiO3）或氟硅酸（H2SiF6）作为二氧化硅源，同时保持温度为20-80℃的条件制备二氧化硅浆料 pH值为6-12; （2）向制备的二氧化硅浆料中加入碱，使二氧化硅与碱的比例为1-25:1，水与碱的比例为50-500至1，并进行 水热反应混合物在100-200℃下进行1-200小时，制备了无机化合物的magadiite或kenyaite; （3）酸化层状无机化合物，在层间形成硅烷醇基团，将其分散到可能与硅烷醇基形成氢键的化合物的有机溶剂中，并通过蒸发干燥所得产物，得到层状 有机化合物; 和（4）在层状有机化合物的层之间插入官能聚合物。
-
公开(公告)号：KR1020040090124A
公开(公告)日：2004-10-22
申请号：KR1020030024052
申请日：2003-04-16
Applicant: 한국화학연구원 , 여수대학교산학협력단
CPC classification number: C04B35/16 , C04B35/553 , C04B35/6303 , C04B2235/5292
Abstract: PURPOSE: A preparation method of magadiite and kenyaite is provided to reduce the production cost due to substitution of the silica source with sodium silicate or fluorosilicate and improve a yield with more simplified and economic process. CONSTITUTION: The preparation method of magadiite and kenyaite comprises: preparing a silica slurry by neutralizing a silica source selected from sodium silicate or fluorosilicate, at 20-80deg.C and pH value of 6-12; adding alkali to the silica slurry to have a molar ratio of silica to alkali being 1-25:1 and water to alkali being 50-500:1; and carrying out hydrothermal reaction at 100-200deg.C for 1-200hours.
Abstract translation: 目的：为了降低硅酸钠或氟硅酸盐代替二氧化硅源的生产成本，提供了麦芽糖盐岩和肯尼亚矿的制备方法，并以更简化和经济的工艺提高了产量。 构成：二氧化硅和肯尼亚的制备方法包括：通过中和硅酸钠或氟硅酸盐的二氧化硅源，20-80℃，pH值为6-12，制备二氧化硅浆料; 向二氧化硅浆料中加入碱以使二氧化硅与碱的摩尔比为1-25:1，水与碱的摩尔比为50-500:1; 并在100-200℃下进行水热反应1-200小时。
-
公开(公告)号：KR100408006B1
公开(公告)日：2003-12-03
申请号：KR1020010033161
申请日：2001-06-13
Applicant: 에스케이 인천정유 주식회사 , 한국화학연구원
IPC: C01B39/02
Abstract: PURPOSE: An improved method for preparing mesoporous crystalline molecular sieve having large pore size and superior hydrothermal stability is provided. CONSTITUTION: The method for preparing mesoporous crystalline molecular sieve comprises the steps of a) preparing a first solution by dissolving 2 to 20 weight parts of silica alone or a mixture of silica and a metal salt or metal alkoxide into 100 weight parts of a hydrogen fluoride solution having concentration of 5 to 50%, wherein a mole ratio of Si/metal is 10 or more; b) preparing a second solution by dissolving 2 to 12 weight parts of cationic surfactant into 100 weight parts of distilled water; c) uniformly mixing the solutions by adding the first solution to the second solution in a weight ratio of 1 to 2:1 (second solution/first solution), and preparing powder by filtering and drying the aged solution after aging the resulting solution at a temperature of 25 to 80 deg.C for 10 to 18 hours by adding 20 to 30 weight parts of concentrated aqueous ammonia (based on 100 weight parts of the hydrogen fluoride solution) to the mixed solution; and d) adding the powder to 200 to 300 weight parts (based on 100 weight parts of the hydrogen fluoride solution) of an ethanol acidic solution, and calcining the resulting material at a temperature of 300 to 600 deg.C for 2 to 4 hours.
Abstract translation: 目的：提供一种制备具有大孔径和优异的水热稳定性的中孔结晶分子筛的改进方法。 构成：制备介孔结晶分子筛的方法包括以下步骤：a）通过将2至20重量份的单独的二氧化硅或二氧化硅与金属盐或金属醇盐的混合物溶解于100重量份的氟化氢 浓度为5至50％的溶液，其中Si /金属的摩尔比为10或更大; b）通过将2至12重量份的阳离子表面活性剂溶解于100重量份的蒸馏水中来制备第二溶液; c）通过将第一溶液以1：2：1的重量比（第二溶液/第一溶液）加入到第二溶液中来均匀地混合溶液，并且通过过滤和干燥老化的溶液来制备粉末， 通过将20至30重量份的浓氨水（基于100重量份的氟化氢溶液）加入到混合溶液中，在25至80℃的温度下进行10至18小时; 和d）将粉末加入到乙醇酸性溶液200-300重量份（基于100重量份氟化氢溶液）中，并将所得材料在300-600℃的温度下煅烧2-4小时 。
-
公开(公告)号：KR100280376B1
公开(公告)日：2001-02-01
申请号：KR1019980032993
申请日：1998-08-14
Applicant: 한국화학연구원
IPC: C01B33/32
Abstract: 본 발명은 결정성 층상 이규산나트륨의 개량된 제조방법에 관한 것으로서, 더욱 상세하게는 일정 조성비의 무수 이규산나트륨 컬릿(cullet)분말을 출발물질로 하여 여기에 바인더로서 물 또는 규산나트륨 수용액을 가하여 조립 입상물을 조제하고 이를 결정화시키는 과정에 최소한의 최종제품을 재순환(recycle)시킴으로써, 연속공정중에 고온의 결정화 조건에서 발생하는 국부적인 소결현상으로 인해 반응물이 결정화 장치 내부에 부착되는 현상을 제거할 수 있을 뿐만 아니라, 최소량의 최종제품만을 재순환함으로써 대량생산시 기존방법에 비해 단위 생산성을 대폭 증가시키는 효과가 있는 결정성 층상 이규산나트륨의 개량된 제조방법에 관한 것이다.
-
公开(公告)号：KR100252463B1
公开(公告)日：2000-04-15
申请号：KR1019970071292
申请日：1997-12-20
Applicant: 한국화학연구원
IPC: B01J20/26
Abstract: PURPOSE: Provided is a manufacturing method of a granular complex agent for wastewater treatment exhibiting molecular sieving effect for the application to advanced wastewater treatment. CONSTITUTION: The manufacturing method of the granular complex agent comprises the steps of blending zeolite 10-70wt.% with activated carbon 10-90wt.%; injecting an alkali metal silicate solution thereto, followed by mixing for granulation; treating the obtained granule with an alkali earth metal salt solution, followed by treating with phosphate solution of 1-10wt.%; washing, filtrating, and drying; calcining the granule under reductive gas conditions ranging from 500 to 800deg.C for 0.5-10hrs.
Abstract translation: 目的：提供用于废水处理的颗粒状复合剂的制造方法，其具有用于高级废水处理的分子筛分效应。 构成：颗粒状复合剂的制造方法包括将10-70wt％的沸石与10-90wt。％活性炭共混的步骤; 向其中注入碱金属硅酸盐溶液，然后混合制粒; 用碱土金属盐溶液处理得到的颗粒，然后用1-10重量％的磷酸盐溶液处理; 洗涤，过滤和干燥; 在500至800℃的还原气体条件下煅烧颗粒0.5-10小时。
-
Patent Agency Ranking
公开(公告)号：KR1019990014990A
公开(公告)日：1999-03-05
申请号：KR1019970036851
申请日：1997-08-01
Applicant: 한국화학연구원
IPC: C01B33/023
Abstract: 본 발명은 층상 나트륨마가다이트의 제조방법에 관한 것으로서, 더욱 상세하게는 실리카원과 알칼리원을 각각 별도로 투입하는 대신에 규산나트륨 수용액을 원료물질로 사용하여 수용액상에서 수열합성시키는 간단한 방법에 의해 나트륨마가다이트로 제조하는 방법으로, 기존방법에 비하여 제품의 순도를 높이고 반응시간을 단축시켜 에너지 소모를 획기적으로 줄일 수 있고, 값싼 원료물질을 사용하고 수율을 극대화함으로써 원가절감 효과를 얻을 수 있는 결정성 층상실리케이트의 일종인 층상 나트륨마가다이트의 제조방법에 관한 것이다.
-
公开(公告)号：KR1019990009359A
公开(公告)日：1999-02-05
申请号：KR1019970031732
申请日：1997-07-09
Applicant: 한국화학연구원
Abstract: 본 발명은 탈취제용 입상 복합 분자체와 그 제조방법에 관한 것으로서, 더욱 상세하게는 각종 형태의 제올라이트와 활성탄의 혼합물에 알칼리 금속 실리케이트 수용액을 배합하여 입상화시킨 복합 분자체 조성물에 구리, 철, 아연 및 알루미늄 등의 활성금속을 담지시킴으로써 악취 원인 가스를 흡착 제거하는 흡착 특성이 우수하고, 획기적인 흡착량 증가로 인한 장기간 사용이 가능하며, 식품 사용에 있어서 신선도 유지 기능 등의 매우 유용한 특성을 가지고 있어서 냉장고, 음식물 쓰레기 처리기, 화학 공장 및 동물 사육장 등에서 발생하는 악취 제거 및 공기 정화에 유용한 탈취제용 입상 복합 분자체와 그 제조방법에 관한 것이다.
-
公开(公告)号：KR1019960007542A
公开(公告)日：1996-03-22
申请号：KR1019940020113
申请日：1994-08-14
Applicant: 한국화학연구원
IPC: C07C217/78
Abstract: 본 발명은 4-클로로-2,5-디알콕시 니트로벤젠을 아세토 니트릴 또는 그의 수용액을 용매로 하여 촉매의 황화처리 여부에 관계없이 백금계 담지 촉매하에 수소환원시켜 탈염소화 없이 4-클로로-2,5-디알콕시 아닐린을 제조하는 방법에 관한 것이며 또한 생성 혼합물을 산석(酸析) 또는 염석(鹽析)을 통해 정제함으로써 반응물의 순도에 관계없이 고순도의 4-클로로-2,5-디알콕시 아닐린을 얻는 정제 방법에 관한 것이다.
-
公开(公告)号：KR1019950031902A
公开(公告)日：1995-12-20
申请号：KR1019950013679
申请日：1995-05-29
Applicant: 한국화학연구원
IPC: C01B33/32
Abstract: 본 발명은 층상결정성 이규산나트륨의 제조방법에 관한 것으로서, 더욱 상세하게는 SiO
2 /Na
2 O이 몰비가 1.80~2.20 범위로 저정되어 생산된 컬릴(cullet)분말을 출발물질로 하여 여기에 소량의 물을 가하여 조립입상물을 먼저 제조하고 이 조립입상물을 소성로에 투입한 다음 소성공정만을 거치는 간단한 방법으로 층상결정성 이규산나트륨을 제조함으로써, 기존방법에 비하여 제품의 순도를 높이고 제조공정을 단순화 하는 한편, 에너지 소모를 획기적으로 줄일 수 있어 원가절감은 물론 장치내에 반응물이 침적되는 현상을 개선하여 물 연화제(water softmer) 또는 세제조성물의 빌더(builder)로서 유용한 층상결정성 이규산나트륨의 새로운 제조방법에 관한 것이다. -
-
-
-
-
-
-
-
-