公开(公告)号：KR1019950010548B1
公开(公告)日：1995-09-19
申请号：KR1019920021497
申请日：1992-11-16
Applicant: 제일모직주식회사
IPC: C08F2/24 , C08F279/00
Abstract: The rubbric latex is prepd. by emulsion polymerization of 70-100 wt.pts. of a conjugated dien type monomer, and/or 30-0 wt.pts. of a vinyl type monomer, 60-150 wt.pts. of an ion exchanging water, and 0.5-10.0 wt.pts. of an emulsifying agent, where a part of the emulsifying agent is added at an early step and the remainder of the emulsifying agent is continueosly added in the reaction. The conjugated dien type monomer is the mixt. comprising one or more of 1,3-butadien, isoprene, 2,3-dimethyl-1,3-butadien, 2-chlorobutadien-1 ! ,3, or 2,3-dichlorobutadien-1,3; and the vinyl type monomer is styrene, vinyl toluene, divinyl benzene, or alpha-methyl styrene.
Abstract translation: 乳胶乳是制备的。 通过70-100重量ppm的乳液聚合。 的共轭二烯型单体，和/或30-0wt.pts。 的乙烯基类单体，60-150重量份。 的离子交换水，和0.5-10.0重量ppm。 的乳化剂，其中一部分乳化剂在早期步骤中加入，剩余的乳化剂在反应中继续加入。 共轭二烯型单体是混合物。 包括一种或多种1,3-丁二烯，异戊二烯，2,3-二甲基-1,3-丁二烯，2-氯丁二烯-1 ，3或2,3-二氯丁二烯-1,3; 乙烯基类单体是苯乙烯，乙烯基甲苯，二乙烯基苯或α-甲基苯乙烯。
-
-
公开(公告)号：KR1019940011506A
公开(公告)日：1994-06-21
申请号：KR1019920021499
申请日：1992-11-16
Applicant: 제일모직주식회사
IPC: C08F285/00
Abstract: 본 발명은 내후성이 우수한 내충격성 무광택 아크릴계고무-스티렌-아크릴로니트릴 수지의 제조방법에 관한 것이다.
본 발명은 2단계 공정을 거쳐 제조된 가교 아크릴계 고무 라텍스 10 내지 60중량부(a)에 스티렌 33 내지 14중량부(b), 아크릴로니트릴 14 내지 4중량부(c)를 그라프트 중합시킨 1차 그라프트 중합체에, 스티렌 34.5 내지 16중량부(b′)와, 아크릴로니트릴 11.5 내지 6중량부(c′)를 프리에멀젼 상태로 만든 후 연속 투입하여 2차 그라프트 중합시키는 것을 특징으로 한다.
본 발명의 방법에 의하여 제조된 수지는 내후성과 무광택성이 요구되는 전기, 전자제품, 자동차용 부품, 농기구등 일광노출이 많은 외장 부품 등에 사용될 수 있다.-
-
-
Patent Agency Ranking
公开(公告)号：KR100100992B1
公开(公告)日：1996-06-21
申请号：KR1019920021498
申请日：1992-11-16
Applicant: 제일모직주식회사
IPC: C08F279/06
-
公开(公告)号：KR1019960005078B1
公开(公告)日：1996-04-20
申请号：KR1019920021493
申请日：1992-11-16
Applicant: 제일모직주식회사
Abstract: To increase the heat resistance and impact resistance of N-phenylmaleimide copolymer, ultra-high molecular weight of N-phenylmaleimide copolymer is prepared and added to the N-phenylmaleimide copolymer and graft copolymer by compounding. The copolymer(A) is made by emulsion polymerization of N-phenylmaleimide, styrene, acrylonitrile. The copolymer(B) is made by same polymerization as above and same monomer is used but the copolymer has ultrahigh molecular weight. The copolymer(C) is graft copolymer that is made of rubber, styrene acrylonitrile by emulsion polymerization. The new styrene-acrylonitrile-N-phenylmaleimide copolymer is prepared by compounding the 35-60 wt.% of copolymer(A), 5-30 wt.% of copolymer(B) and 20-50 wt.% of graft copolymer(C). This polymer does not lose the mechanical property, shows a good heat resistance of styrene-acrylonitrile copolymer, and increases the heat deformation temperature of ABS resin as a resulting polymer.
Abstract translation: 为了提高N-苯基马来酰亚胺共聚物的耐热性和耐冲击性，制备了超高分子量的N-苯基马来酰亚胺共聚物，并通过配混添加到N-苯基马来酰亚胺共聚物和接枝共聚物中。 共聚物（A）通过N-苯基马来酰亚胺，苯乙烯，丙烯腈的乳液聚合制备。 共聚物（B）通过与上述相同的聚合制备，使用相同的单体，但共聚物具有超高分子量。 共聚物（C）是通过乳液聚合由橡胶，苯乙烯丙烯腈制成的接枝共聚物。 通过将35-60重量％的共聚物（A），5-30重量％的共聚物（B）和20-50重量％的接枝共聚物（C）的共混物 ）。 该聚合物不失去机械性能，表现出良好的苯乙烯 - 丙烯腈共聚物的耐热性，并且增加作为所得聚合物的ABS树脂的热变形温度。
-
-
公开(公告)号：KR1019940011573A
公开(公告)日：1994-06-21
申请号：KR1019920021494
申请日：1992-11-16
Applicant: 제일모직주식회사
Abstract: 본 발명은 알파-메틸스티렌을 사용한 내열성 ABS의 후처리 공정을 개선함으로서 최종 생산제품의 물성을 향상시킨 열가소성 수지 조성물의 제조방법에 관한 것이다.
본 발명은 스티렌-아크릴로니트릴 공중합체(SAN) 50-70부, 그라프트 공중합체 50-30부로 구성된 내열 ABS 수지에 있어서, SAN 라텍스와 그라프트 공중합체 라텍스를 제조후 1차로 라텍스 블렌딩을 실시하고, 2차로 부족성분을 분말상으로 추가 블렌딩하는 것을 특징으로 한다.
본 발명의 방법에 의하여 제조된 수지 조성물은 물성과 강도가 동시에 요구되는 분야에서 적절히 사용될 수있다.-
20.发明公开충격 보강제용 열가소성 수지 조성물과 그 제조방법 및 이 조성물을 함유한 내충격성 염화비닐계 수지 조성물 失效抗冲击改性剂用热塑性树脂组合物，其制造方法以及含有该组合物的耐冲击性氯乙烯树脂组合物
公开(公告)号：KR1019940011508A
公开(公告)日：1994-06-21
申请号：KR1019920021498
申请日：1992-11-16
Applicant: 제일모직주식회사
IPC: C08F279/06
Abstract: 본 발명은 충격보강제로 사용될 수 있는 열가고성 수지 조성물 및 그 제조방법에 관한 것이다.
본 발명은 수지의 온도조건이 상온과 저온으로 바뀌는 조건하에서도 양호한 충격 보강효과를 나타내며, 소량의 첨가로 우수한 충격보강효과를 나타내고, 광택이 양호한 열가소성 수지 조성물을 제공하는 것을 목적으로 한다.
본 발명은 디엔계 고무질 중합체에 방향족 비닐계 단량체를 첨가하여 1차 그라프트 중합 후, 2종 이상의 메타크릴산 알킬에스테르 혼합물을 첨가하여 2차 그라프트 중합시키는 것을 특징으로 한다.
-
-
-
-
-
-
-
-
-