公开(公告)号：KR100816039B1

公开(公告)日：2008-03-21

申请号：KR1020070017164

申请日：2007-02-20

Applicant: 한국교통대학교산학협력단

Inventor： 윤만순 ,  어순철

IPC: H01L41/187

CPC classification number: H01L41/1871 ,  H01L41/1873 ,  H01L41/37

Abstract: A BNBT-based piezoelectric ceramic is provided to form a single perovskite solid solution phase in which a pyrochlore phase doesn't exist, by adding CaO. Material powder of Bi2O3, Na2CO3, BaCO3, TiO2 and CaO of 0.01 weight percent is prepared to form a composition of (Bi0.5Na0.5)0.94Ba0.06TiO3. A ball milling process and a dry process are performed on the material powder for a time interval of 24 hours by using zirconia ball and deionized water. After the dried material powder is classified into 100 mesh or less, a calcination process is performed at a temperature of 1115.8-1123K by using an alumina crucible. After the calcinated powder material is roughly ground in an alumina mortar, the calcinated powder material is wet-ground by using alcohol of 99.9 percent wherein a PVB(polyvinyl butyral co-vinyl) coupling agent is added 20 minutes before the grinding process is completed. After the ground powder material is heated, stirred and dried, the dried powder is classified into 80 mesh.

Abstract translation: 通过添加CaO，提供基于BNBT的压电陶瓷，以形成其中不存在烧绿石相的单一钙钛矿固溶体相。 制备Bi2O3，Na2CO3，BaCO3，TiO2和CaO的物质粉末0.01重量％，形成（Bi0.5Na0.5）0.94Ba0.06TiO3的组成。 通过使用氧化锆球和去离子水，对材料粉末进行24小时的球磨和干法处理。 将干燥后的原料粉末分级为100目以下，通过使用氧化铝坩埚，在1115.8-1123K的温度下进行煅烧。 煅烧后的粉末材料在氧化铝砂浆中粗磨后，用99.9％的醇将煅烧后的粉末材料进行湿磨，其中在研磨过程完成20分钟之前加入PVB（聚乙烯醇缩丁醛共聚乙烯基）偶联剂。 将粉末状粉末加热，搅拌干燥后，将干燥粉末分为80目。

公开(公告)号：KR1020160069769A

公开(公告)日：2016-06-17

申请号：KR1020140175790

申请日：2014-12-09

Applicant: 한국교통대학교산학협력단

Inventor： 어순철 ,  윤만순

IPC: C01B25/45 ,  C01G49/00 ,  C01D15/00 ,  H01M4/58 ,  H01M10/0525

CPC classification number: C01B25/45 ,  C01B25/37 ,  C01D15/00 ,  C01G49/00 ,  H01M4/58 ,  H01M10/0525

Abstract: 본발명은상대적으로저가인출발물질을사용하여리튬인산철활물질을제조하는방법에관한것으로, Fe(NO)를출발물질로하여 FePO를합성하는단계; 및상기 FePO와리튬소스물질을함께볼 밀링하여 LiFePO를합성하는단계를포함한다. 본발명은, 상대적으로저가의물질인 Fe(NO)를출발물질로사용함으로써, LiFePO캐소드활물질의제조비용을낮출수 있는효과가있다. 또한, 먼저출발물질인 Fe(NO)를사용하여 FePO를합성한뒤에이를사용하여 LiFePO를제조함으로써, 전기화학적특성이뛰어난활물질을제공할수 있는효과가있다.

Abstract translation: 本发明涉及一种使用相对便宜的原料制备磷酸铁锂活性物质的方法，该方法包括以Fe（NO 3）3原料合成FePO 4; 并用锂源材料球磨FePO_4以合成LiFePO_4。 本发明通过使用相对廉价的Fe（NO 3）3起始材料，具有降低LiFePO 4的正极活性物质的制造成本的效果。 此外，本发明通过使用Fe（NO 3）3的起始材料合成FePO 4，然后通过使用FePO 4制备LiFePO 4，从而具有提供具有优异的电化学性能的活性材料的效果。

公开(公告)号：KR101537297B1

公开(公告)日：2015-07-22

申请号：KR1020130107461

申请日：2013-09-06

Applicant: 한국교통대학교산학협력단

Inventor： 윤만순 ,  어순철 ,  이영근

IPC: H01M4/583 ,  H01M4/58

Abstract: 본발명은리튬이온을과량으로첨가하여전기적특성을향상시킬수 있는리튬이차전지캐소드용 LiFePO/C 복합재제조방법에관한것이다. 본발명에따른리튬이차전지캐소드용 LiFePO/C 복합재제조방법은, Fe 전구체, 리튬소스및 탄소소스를혼합하는단계; 및상기 FePO, 리튬소스및 카본소스가혼합된혼합물을볼 밀하여 LiFePO/C(x=0.008 내지 0.012)를합성하는단계;를포함하는것을특징으로한다.

公开(公告)号：KR1020150003593A

公开(公告)日：2015-01-09

申请号：KR1020130076653

申请日：2013-07-01

Applicant: 한국교통대학교산학협력단

Inventor： 윤만순 ,  어순철 ,  이영근

IPC: C04B35/64 ,  C04B35/495

CPC classification number: C04B35/495 ,  C04B35/62615 ,  C04B35/6262 ,  C04B35/64 ,  C04B2235/3251 ,  C04B2235/442

Abstract: 고에너지 나노 밀을 이용한 NKLN 세라믹스 및 그 제조 방법에 대하여 개시한다.
본 발명에 따른 NKLN 세라믹스 제조 방법은 Na
0.475 K
0.475 Li
0.05 NbO
3 (이하, NKLN)을 합성하기 위한, 나트륨(Na), 칼륨(K), 리튬(Li) 및 니오븀(Nb) 중 하나 이상을 포함하는 출발물질들을 칭량하여 혼합하는 단계; 상기 혼합된 출발물질들을 고에너지 나노 밀을 이용하여 1차 분쇄하는 단계; 상기 1차 분쇄된 결과물을 하소하는 단계; 상기 하소된 결과물을 2차 분쇄하는 단계; 상기 2차 분쇄된 결과물을 성형하여 성형체를 형성하는 단계; 및 상기 성형체를 소결하는 단계;를 포함하는 것을 특징으로 한다.

Abstract translation: 公开了使用高能纳米微粒的Na0.475K0.475Li0.05NbO3（NKLN）陶瓷及其制造方法。 制造NKLN陶瓷的方法包括以下步骤：称量用于合成包含钠（Na），钾（K），锂（Li）和铌（Nb）中的一种或多种的NKLN的起始材料并将其混合; 主要使用高能纳米颗粒研磨混合起始材料; 煅烧主要研究结果; 二次研磨煅烧结果; 通过模拟二次研磨结果形成模制体; 并烧结成型体。

公开(公告)号：KR101029027B1

公开(公告)日：2011-04-15

申请号：KR1020090002692

申请日：2009-01-13

Applicant: 한국교통대학교산학협력단

Inventor： 윤만순 ,  이영근 ,  어순철

IPC: H01L41/187 ,  C04B35/475 ,  B82Y40/00

Abstract: 본 발명은 친환경 무연계 압전세라믹스인 BNBT6 압전세라믹스에 관한 것으로, 더욱 자세하게는 압전 및 유전 특성이 향상된 BNBT6 압전세라믹스 및 그의 제조방법에 관한 것이다.
본 발명에 의한 BNBT6 압전세라믹스는, 페로브스카이트 결정구조를 갖는 BNBT계 압전세라믹스에 있어서, 조성이 (Bi
0.5 Na
0.5 )
0.94 Ba
0.06 TiO
3 이며, 입자의 크기가 50~70㎚의 범위인 것을 특징으로 한다.
또한 본 발명에 의한 BNBT6 압전세라믹스의 제조방법은, BNBT6 압전세라믹스의 조성에 맞추어 BaTiO
3 , TiO
2 , Na
2 CO
3 및 Bi
2 O
3 원료분말을 준비하는 단계; 상기 원료분말을 혼합하여 볼 밀링하는 단계; 상기 밀링된 분말을 하소하는 단계; 상기 하소된 분말을 나노 밀링하는 단계를 포함하는 것을 특징으로 한다.
압전세라믹스, 압전소자, BNBT, BNBT6, BNBT6 압전세라믹스

公开(公告)号：KR100933718B1

公开(公告)日：2009-12-24

申请号：KR1020080032250

申请日：2008-04-07

Applicant: 한국교통대학교산학협력단

Inventor： 윤만순 ,  이영근 ,  어순철

IPC: C04B35/00 ,  H01L41/187

Abstract: 본 발명은 BNBT계 압전세라믹스와 그 제조방법에 관한 것이다. 본 발명의 BNBT계 압전세라믹스는, (Bi
0.5 Na
0.5 )
0.94 Ba
0.06 TiO
3 에 CaO 및 MnO가 첨가되어 형성된 것을 특징으로 한다.
본 발명에 의한 BNBT계 압전세라믹스는 납이 함유되지 않은 친환경 압전소재인 BNBT계 압전세라믹스에 CaO와 MnO를 동시 첨가함으로써, BNBT계 압전세라믹스의 유전상수(d
33 ), 전기기계결합계수(k
p ) 및 비유전율(K
33
T ) 등의 특성뿐만 아니라 소결밀도, 기계적품질계수(Q
m ) 및 강유전체상의 안정도 등의 특성을 향상된다. 또한, 본 발명의 BNBT계 압전세라믹스는 CaO 및 MnO의 첨가비율을 조절함으로써 적용 분야의 목적에 맞도록 상기 특성들이 조절된 다양한 특성의 BNBT계 압전세라믹스를 제조할 수 있다.
BNBT 압전세라믹스, 페로브스카이트, CaO, MnO

Abstract translation: 目的：提供BNBT压电陶瓷及其制造方法，以通过向BNBT压电陶瓷中添加CaO和MnO来提高介电常数，机电耦合系数，烧结密度，机械品质因数和铁电稳定性。 构成：BNBT压电陶瓷具有钙钛矿结构。 BNBT压电陶瓷是通过向（Bi0.5Na0.5）0.94Ba0.06TiO3中添加CaO和MnO而制成的。 CaO和MnO的含量是xwt％和ywt％，x和y满足不等式0＆lt; x + y＆amp; lt; = 0.1。

公开(公告)号：KR100801109B1

公开(公告)日：2008-02-05

申请号：KR1020060086068

申请日：2006-09-07

Applicant: 한국교통대학교산학협력단

Inventor： 윤만순 ,  어순철

IPC: H05B41/26 ,  H05B41/14 ,  H05B41/38

CPC classification number: H05B41/2806 ,  H05B41/282 ,  H05B41/2822

Abstract: An EEFL(External Electrode Fluorescent Lamp) drive circuit using a balun transformer is provided to compensate brightness difference of both electrodes of the EEFL by applying the same amount of voltage to both ends of a load and driving load resistance in both ends of the balun transformer. An EEFL drive circuit using a balun transformer comprises a function generator(303), a power amplifier(306), an impedance matching unit(309), a piezoelectric transformer(312), the balun transformer, and an EEFL. The function generator generates and supplies a pulse signal with a predetermined frequency. The power amplifier amplifies the pulse signal received from the function generator. The impedance matching unit is connected to an output terminal of the power amplifier. A common terminal of the piezoelectric transformer is grounded and an input terminal thereof is connected to the impedance matching unit. The balun transformer converts a single-wire type output signal from the piezoelectric transformer into a two-wire type signal. The EEFL is applied with driving power from the balun transformer.

Abstract translation: 提供使用平衡 - 不平衡变压器的EEFL（外部电极荧光灯）驱动电路，通过在负载两端施加相同的电压和平衡不平衡变压器两端的驱动负载电阻来补偿EEFL的两个电极的亮度差 。 使用平衡不平衡变压器的EEFL驱动电路包括功能发生器（303），功率放大器（306），阻抗匹配单元（309），压电变压器（312），平衡不平衡变压器和EEFL。 函数发生器产生并提供具有预定频率的脉冲信号。 功率放大器放大从功能发生器接收的脉冲信号。 阻抗匹配单元连接到功率放大器的输出端。 压电变压器的公共端子接地，其输入端子连接到阻抗匹配单元。 平衡不平衡变压器将压电变压器的单线式输出信号转换为双线型信号。 EEFL适用于平衡不平衡变压器的驱动电源。

公开(公告)号：KR100663971B1

公开(公告)日：2007-01-02

申请号：KR1020050078357

申请日：2005-08-25

Applicant: 한국교통대학교산학협력단 ,  고려전자주식회사

Inventor： 어순철 ,  김일호 ,  윤만순 ,  김영민 ,  박희법

IPC: C04B35/491 ,  C04B35/493

Abstract: PNN-PZT piezoelectric ceramics with constant content of NiO are provided to have dielectric and piezoelectric properties such as piezoelectric charge constant and are preferably used for accelerometer sensors by comprising PbO, TiO2, NiNb2O6 and ZrO2 and adding NiO in desired content to the ceramics. The piezoelectric ceramics are formed by steps of: preparing each of PbO, ZrO2, TiO2 and NiNb2O6 powders as starting materials; calcining the starting materials, NiO and Nb2O5; milling all of the starting materials then drying the milled powders; sizing and calcining the dried powders; adding additives to the powders after crushing the calcined powders; and milling the mixture. The obtained ceramics contain NiO in solid solution form and has perovskite crystalline structure and composition of 0.5Pb(Zr0.52Ti0.48)O30.5Pb(Ni1/3Nb2/3)O3-y[mol%]NiO-1[wt%]PbO wherein y is 1.0.

Abstract translation: 提供具有恒定含量的NiO的PNN-PZT压电陶瓷以具有诸如压电电荷常数的电介质和压电性能，并且优选用于通过包括PbO，TiO 2，NiNb 2 O 6和ZrO 2并将所需内容物中的NiO添加到陶瓷中的加速度计传感器。 压电陶瓷由以下步骤形成：以PbO，ZrO2，TiO2和NiNb2O6粉末为原料， 焙烧原料NiO和Nb2O5; 研磨所有起始材料，然后干燥研磨的粉末; 上浆和煅烧干粉; 在粉碎煅烧粉末后，向粉末中添加添加剂; 并研磨混合物。 得到的陶瓷含有固溶体形式的NiO，具有钙钛矿晶体结构，组成为0.5Pb（Zr0.52Ti0.48）O30.5Pb（Ni1 / 3Nb2 / 3）O3-y [mol％] NiO-1 [wt％] 其中y为1.0。

公开(公告)号：KR101682381B1

公开(公告)日：2016-12-05

申请号：KR1020150036077

申请日：2015-03-16

Applicant: 한국교통대학교산학협력단

Inventor： 어순철 ,  윤만순

IPC: C01B25/45 ,  C01B31/02 ,  H01M10/0525

Abstract: 본발명은전기화학적특성이뛰어난탄소코팅리튬인산철의제조방법으로서, 염화철이용하여인산철수화물분말을제조하는단계; 상기인산철수화물분말과리튬소스물질을혼합하여고상법으로전구체를제조하는단계; 상기전구체에탄소소스물질을첨가하여고에너지나노밀링하는단계; 및상기고에너지나노밀링하는단계에서얻어진수득물을건조및 소성하는단계를포함한다. 따라서본 발명에따른탄소코팅리튬인산철의제조방법은짧은공정시간, 비용절감및 전기적특성이향상된친환경적인탄소코팅리튬인산철을제공하는효과가있다.

Abstract translation: 本发明涉及具有优异的电化学性能的涂覆有碳酸锂的磷酸锂金属的制造方法。 该方法包括以下步骤：使用氯化铁生产磷酸铁水合物粉末; 通过混合磷酸铁水合物粉末和锂源材料，使用固相法制备前体; 通过在前体中添加碳源材料进行高能纳米 - 并干燥和煅烧在高能纳米级步骤中获得的产物。 涂覆有碳酸锂的磷酸锂的制备方法提供了环氧锂金属磷酸盐，涂覆了碳，工艺时间短，成本降低，电性能改善。

公开(公告)号：KR101454341B1

公开(公告)日：2014-10-27

申请号：KR1020130121715

申请日：2013-10-14

Applicant: 한국교통대학교산학협력단

Inventor： 윤만순 ,  어순철 ,  이영근

IPC: H01L41/187

CPC classification number: H01L41/1876 ,  H01L41/43

Abstract: Disclosed are a piezoelectric ceramic capable of increasing a g33 value by maintaining a low-K (dielectric constant), and having a high d33 value without reducing a phase transition temperature (Tc) by adding BiYO_3 having a low-K to Pb(Zr_0.53Ti_0.47)O_3 and a method of fabricating the same. According to the present invention, the piezoelectric ceramic is expressed by the following chemical formula 1. [Chemical formula 1] (1-x) (Zr_0.53Ti_0.47)O_3 -x BiYO_3 (here, 0

Abstract translation: 公开了通过将具有低K的BiYO 3添加到Pb（Zr_0）中，能够通过保持低K（介电常数）来增加g33值并且具有高d33值而不降低相变温度（Tc）的压电陶瓷。 53Ti_0.47）O_3及其制造方法。 根据本发明，压电陶瓷由以下化学式1表示。[化学式1]（1-x）（Zr_0.53Ti_0.47）O_3-x BiYO_3（这里，0