Abstract: PURPOSE: A porous titanium-hydroxyapatite(ha) composite and a manufacturing method thereof are provided to prevent cell death and to enable efficient cell proliferation and cell fixation by sintering and leaching titanium and hydroxyapatite. CONSTITUTION: A manufacturing method of a porous titanium-hydroxyapatite(ha) composite comprises the following steps: mixing titanium (Ti) powder and hydroxyapatite powder; forming a composite by sintering the mixed powder; and adding the composite to a leaching solution and forming a pore by eluting the hydroxyapatite. A particle size of the titanium powder is 5-100 micro meters and the hydroxyapatite powder is 5-100 nano meters. 10-50 weight% of the hydroxyapatite powder is mixed in the titanium powder. The sintering step is processed under 10-200 MPa, at 800-1200 deg. Celsius for 2-10 minutes. The porous titanium-hydroxyapatite composite comprises micro sized pores which are connected as 3D.

Abstract translation: 目的：提供多孔钛羟基磷灰石（ha）复合物及其制备方法，以防止细胞死亡，并能通过烧结和浸出钛和羟基磷灰石使细胞增殖和细胞固定。 构成：多孔钛羟基磷灰石（ha）复合材料的制造方法包括以下步骤：将钛（Ti）粉末和羟基磷灰石粉末混合; 通过烧结混合粉末形成复合材料; 并将该复合物加入到浸出溶液中并通过洗脱羟基磷灰石形成孔。 钛粉末的粒径为5-100微米，羟基磷灰石粉末为5-100纳米。 将10-50重量％的羟基磷灰石粉末混合在钛粉末中。 烧结步骤在10-200MPa，800-1200℃加工。 摄氏2-10分钟。 多孔钛羟基磷灰石复合材料包括以3D连接的微孔。

公开(公告)号：KR101239112B1

公开(公告)日：2013-03-06

申请号：KR1020100135468

申请日：2010-12-27

Applicant: 전북대학교산학협력단

Inventor： 우기도 ,  강덕수

IPC: C04B38/04 ,  C04B35/64 ,  A61L27/06

Abstract: 본 발명은 티타늄과 수산화인회석의 혼합물을 소결 및 침출하여 세포와의 결합력을 높인 표면 다공성의 티타늄-수산화인회석 복합체 및 이의 제조방법에 관한 것이다. 본 발명에 의한 표면 다공성 티타늄-수산화인회석 복합체는 뼈와 유사한 저 탄성계수를 가지며, 또한 HA코팅 시 HA코팅 층이 박리되는 문제를 해소하여 우수한 생체적합성을 가진다. 본 발명의 복합체는 3차원적으로 연결된 마크로 사이즈의 기공이 다수 형성되어 있어 효율적인 세포 증식 및 고정, 세포괴사를 방지할 수 있다.